In this study, block copolymer of polystyrene and polyethylene glycol methyl ether methacrylate(PEGMA) by ATRP(atom transfer radical polymerization) method was synthesized. 4 arm-molecule which contained halogen atom was synthesized for an initiator. With 4 arm-molecule monodispered polystyrene were synthesized by ATRP method. The molecular change of synthesized monodispersed polystyrene with respect to time was investigated and living polymer characteristic was confirmed. Block copolymer of polystyrene and polyethylene glycol methyl ether methacrylate(PEGMA) was synthesized by ATRP with macroinitiator which was synthesized from the monodispersed polystyrene(Mn=12000). The molecular weight of obtained PS-b-PEGMA was 22,000.

폴리비닐리덴플로라이드(PVDF) 지지체 위에 빗살모양의 술폰화된 공중합체를 코팅하여 나노 분리막을 제조하였다. 빗살모양의 공중합체는 원자전달 라디칼 중합법(ATRP)에 의해 제조하였으며, 폴리비닐클로라이드의 주사슬과 폴리스티렌 술폰산(PSSA)의 곁사슬로 구성되어 있다. 핵자기 공명법(1 H-NMR), FT-IR분광학 그리고 WAXS 분석법에 의해 공중합체가 성공적으로 합성되었음을 확인하였다 PVC-g-PSSA로 구성된 복합 나노 분리막은 PSSA의 함량이 증가함에 따라 플럭스와 배제율 모두 증가하였다. 이러한 성능 향상은 분리막의 술폰산의 함량의 증가로써 설명할 수 있다. PSSA가 71wt%첨가된 나노 복합막의 배제율은 Na2SO4 88%, NaCl 33%을 나타내었고, 플럭스는 Na2SO4 26, NaCl 34 L/m 2 h을 각각 나타내었다.