High voltage impulse(HVI) has been gained attention as an alternate technique controlling CaCO3 scale formation. Investigation of key operational parameters for HVI is important, however, those had not been reported yet. In this study, the effect of temperature and applied voltage of HVI on Ca2+ concentration was studied. As the applied voltage from 0 to 15kV and the temperature increased from 20 to 60°C, the Ca2+ concentration decreased, indicating that the aqueous Ca2+ precipitated to CaCO3. The Ca2+ concentration decreased up to 81% under the condition of 15kV and 60°C. Rate constant for the precipitation reaction, k was determined under different temper1ature and voltage. The reaction rate constant under the 15kV and 60°C condition was evaluated to 66☓10-3 L/(mmol·hr), which was 5 times greater than the k of the reaction without HVI at same temperature. The increases in k by HVI at higher temperature region(40 to 60°C) was much greater than at lower temperature region(20 to 40°C), which implies temperature is more important parameter than voltage for reducing Ca2+ concentration at high temperature region. These results show that the HVI induction accelerates the precipitation to CaCO3, particularly much faster at higher temperature.

본 연구에서는 칼슘 이온 제거를 위해 칼슘용액에 임계미셀농도(CMC) 이상으로 음이온계면활성제인 sodium dodecyl sulfate (SDS)를 주입하여 미셀을 형성한 후, 미셀 표면에 칼슘 이온의 흡착 또는 결합으로 형성된 응집체들을 2종류의 세라믹 분리막으로 배제하였다. 그 결과, 99.98% 이상 칼슘 배제율을 보였다. 또한 본 실험범위에서 TMP가 증가할수록 막오염(Rf)은 증가하는 경향을 보였지만, 구동력의 증가로 인해 총여과부피(VT) 및 무차원한 투과선속(J/Jo), 투과선속(J) 역시 증가하였다. 또한 세라믹 분리막에 대하여 주기적 질소 역세척을 실시할 경우, 질소 역세척 시간(BT) 및 여과 시간(FT), 즉 역세척 주기의 영향을 조사하였다. 그 결과, NCMT-6231 (평균기공 0.07 μm) 및 NCMT-7231 (0.10 μm) 분리막의 최적 BT는 각각 10초, 15초이었다. 또한, 최적 FT는 2종류 분리막 모두 5분으로, 빈번한 질소 역세척이 막오염을 효과적으로 감소시켰다. 한편 칼슘용액으로 실험하여 도출된 최적 운전조건을 두유 포장팩 세척수로 사용하고 있는 지하수에 적용한 결과, 2종류의 분리막 모두 칼슘을 99.98% 이상 제거할 수 있었다.

This study evaluated the biosorption properties of calcium ion using Aerobic Granular Sludge (AGS). A sequencing batch reactor was used to induce the production of Extracellular Polymeric Substances (EPS) through salinity injection, and the calcium ion adsorption efficiency was analyzed by a batch test. The EPS contents showed significant changes (104-136 mg/g MLVSS) at different salinity concentrations. The calcium ion adsorption efficiency was highest for AGS collected at 5.0% salinity, and it was confirmed that the biosorption efficiency of AGS was increased owing to the increase in EPS content. The results of the Freundlich isotherms showed that the ion binding strength (1/n) was 0.3941-0.7242 and the adsorption capacity (Kf) was 2.4082-3.3312. The specific surface area and the pore size of the AGS were 586.1 m2/g and 0.7547 nm, respectively, which were not significantly different from each other. It was confirmed that the influence of biological properties, such as EPS content, was relatively large among the factors affecting calcium ion adsorption.

In this study, the effect of calcium leaching on chloride ion penetration resistance of mortar specimens was evaluated. According to test results, the penetration depth of chloride ion was increased after the calcium leaching attack.

When ginseng seedlings are cultured in paddy fields, quality degradation and yield reduction are induced by severe plant loss with chlorosis on leaves occurred physiological disorder by excessive salt and poor drainage, rusty-root occurrence, and root rot etc. Accordingly, in order to solve these problems, this study was performed to investigate the treatment method, concentrations and time of activated ion calcium as environment-friendly agricultural materials. Activated ion calcium is an enriched and purified water-soluble mineral calcium component for absorbing quickly into plant as a highly functional calcium and it is an alkaline calcium of 37% (370 ml/1 l) concentration with pH 13. Treatment method was that ginseng seeds were sown after removing water in the shade after seed immersion for 1 minute with active ion calcium of 20-fold diluted solution, and then irrigated 4l per 3.3 m2 with 200-fold, 400-fold, and 600-fold diluted solution before emergence on late March, and supplied 1 time on leaves with 500-fold diluted solution in June and July respectively. The disease rate by treatment of activated ion calcium was that on the treatment of soil irrigated with 200-fold diluted solution compared to non-treated soil, damping-off was 33%, anthracnose was 100% reduced and the occurrence rate of rusty-root was 30% reduced. In addition, when active ion calcium of 200-fold diluted solution were soil irrigated, first and second grade ginseng were respectively 26% and 22% produced more, compared with control.

세포내 칼슘은 다양한 세포에서 중요한 생리적 반응을 일으키며, ruthenium red와 ryanodine은 중요한 칼슘 조절자로 작용한다. Ruthenium red는 세포내 칼슘 저장고에서의 calcium induced calcium release(CICR)를 저해한다. Ryanodine은 ryanodine 통로를 통한 칼슘 방출을 촉진한다. 본 실험은 두 조절자가 생쥐 난자와 초기배아의 세포내 칼슘이온 농도에 영향을 미치는지 여부와 그 유효농도를 알