Pollution of chloride ion-reinforced concrete can trigger active corrosion processes that reduce the useful life of structures. Multifunctional materials used as a counter-electrode by electrochemical techniques have been used to rehabilitate contaminated concrete. Cement-based pastes added to carbonaceous material, fibers or dust, have been used as an anode in the non-destructive Electrochemical Chloride Extraction (ECE) technique. We studied the performance of the addition of Carbon Fiber (CF) in a cement-graphite powder base paste used as an anode in ECE of concretes contaminated with chlorides from the preparation of the mixture. The experimental parameters were: 2.3% of free chlorides, 21 days of ECE application, a Carbon Fiber Volume Fraction (CFVF) of 0.1, 0.3, 0.6, 0.9%, a lithium borate alkaline electrolyte, a current density of 4.0 A / m2 and a cement/graphite ratio of 1.0 for the paste. The efficiency of the ECE in the traditional technique using metal mesh as an anode was 77.6% and for CFVF of 0.9% it was 90.4%, with a tendency to increase to higher percentages of the CFVF in the conductive cement-graphite paste, keeping the pH stable and achieving a homogeneous ECE in the mass of the concrete contaminated with chlorides.

공극구조 분석 방법은 ASTM C 457의 리니어트레버스 포인트카운트법이 있으나, 이러한 방법들은 분석하는데 시간과 노력이 너무 많이 소요되어 현재에는 거의 사용되어지지 않고 있다. 근래에는 현미경과 디지털 카메라, 컴퓨터의 프로그램 발달로 화상분석법이 많은 연구자에 의해 연구되고 있다. 본 연구에서는 화상분석법을 통하여 라텍스개질 콘크리트의 공극 구조 특성을 분석하고자 시멘트 종류(보통포틀랜드시멘트, 초속경시멘트)와 라텍스 혼입율(0,15%)에 따라 실험을 수행하였다. 실험결과, 라텍스는 경화 후 콘크리트에서 AE제의 공기연행효과보다 더 우수한 연행공기 량을 갖는 것으로 나타났다. 또한, 화상분석법을 이용할 경우 경화 후 콘크리트 내부 공극 구조에 대한 다양한 정보를 분석할 수 있을 것으로 판단되었다.