Feasibility is investigated for reduction of chromium ore by Si sludge with mixed silicothermic and carbothermic reaction. The reduction behavior of chromium ore using Si sludge is investigated precisely to determine the effects of carbon addition, reaction time, and reaction temperature. The pellets are dropped into the furnace after temperature stabilized. As the amount of C addition increases, the amounts of CO and CO2 gas generation increase. After the dropping of the pellets, the pellets are heated and the reaction starts at about 1,573 K or higher. The pellets maintain their shape until 10 min after the drop, and then melted. As the holding time increased, the size of the reduced metal particles increased. The chromium ore is rapidly reduced by the Si sludge, and the slag penetrated into the chromium ore and reduction progressed inside. As the reduction temperature increased, the reaction initiation time is shortened and the reaction fraction of the reduction reaction increased. As the reaction temperature increased, agglomeration of reduced ferrochrome metal is promoted.

Pechini방법으로 제조한 La0.8Ca0.2CrO3CLC소결체와 La0.8Ca0.2CrO3CLC-Green체를 YSZ에 적층한 후 온도의 함수로 계면에서의 미세구조와 성분이동 등의 거동을 고찰하였다. CLC-G/CLC와 CLC/YSZ계면에서의 CLC면은 반응온도에 상관없이 XRD 관찰에서 주상은 La1-x CaxCrO3그리고 CLC와 반응하지 않은 YSZ면의 결정 상은 cubic-ZrO2으로 각각 나타났다. CLC/YSZ반응 계면의 성분이동은 Zr > La>>Cr>>>Ca 순이었으며, 온도에 따른 개개 성분의 이동도 차이는 크지 않았다. CLC/YSZ계면간의 결합은 계면성분간의 과다한 성분이동 없이 현 연구의 온도전체에 걸쳐 가능한 것으로 나타났다. CLC-G/CLC간의 SEM미세구조는 결합 면을 경계로 저온에서는 결정의 입자크기 차이를 보이다가 온도가 증가할수록 균일화되는 경향을 보였다.였다. 보였다.였다.