The electrochemical reaction between lead borate glass frit doped with Sn metal filler and Ni-Cr wire of a J-type resistor during a term of Joule heating is investigated. The fusing behavior in which the Ni-Cr wire is melted is not observed for the control group but measured for the Sn-doped specimen under 30 V and 500 mA. The Sn-doped lead borate glass frit shows a fusing property compared with other metal-doped specimens. Meanwhile, the redox reaction significantly contributes to the fusing behavior due to the release of free electrons of the metal toward the glass. The electrons derived from the glass, which used Joule heat to reach the melting point of Ni-Cr wire, increase with increasing corrosion rate at interface of metal/ glass. Finally, the confidence interval is 95 ± 1.959 %, and the adjusted regression coefficient, R in the optimal linear graph, is 0.93, reflecting 93% of the data and providing great potential for fusible resistor applications.

As a case study on aspect ratio behavior, Kaolin, zeolite, TiO2, pozzolan and diatomaceous earth minerals are investigated using wet milling with 0.3 mm media. The grinding process using small media of 0.3 pai is suitable for current work processing applications. Primary particles with average particle size distribution D50, ~6 μm are shifted to submicron size, D50 ~0.6 μm after grinding. Grinding of particles is characterized by various size parameters such as sphericity as geometric shape, equivalent diameter, and average particle size distribution. Herein, we systematically provide an overview of factors affecting the primary particle size reduction. Energy consumption for grinding is determined using classical grinding laws, including Rittinger's and Kick's laws. Submicron size is obtained at maximum frictional shear stress. Alterations in properties of wettability, heat resistance, thermal conductivity, and adhesion increase with increasing particle surface area. In the comparison of the aspect ratio of the submicron powder, the air heat conductivity and the total heat release amount increase 68 % and 2 times, respectively.

As a case study on aspect ratio behavior, Kaolin, zeolite, TiO2, pozzolan and diatomaceous earth minerals are investigated using wet milling with 0.3 pai media. The grinding process using small media of 0.3 pai is suitable for current work processing applications. Primary particles with average particle size distribution D50, ~6 μm are shifted to submicron size, D50 ~0.6 μm, after grinding. Grinding of particles is characterized by various size parameters such as sphericity as geometric shape, equivalent diameter, and average particle size distribution. Herein, we systematically provide an overview of factors affecting the primary particle size reduction. Energy consumption for grinding is determined using classical grinding laws, including Rittinger's and Kick's laws. Submicron size is obtained at maximum frictional shear stress. Alterations in properties of wettability, heat resistance, thermal conductivity, and adhesion increase with increasing particle surface area. In the comparison of the aspect ratio of the submicron powder, the air heat conductivity and the total heat release amount increase 68 % and 2 times, respectively.

Pechini방법으로 제조한 La0.8Ca0.2CrO3CLC소결체와 La0.8Ca0.2CrO3CLC-Green체를 YSZ에 적층한 후 온도의 함수로 계면에서의 미세구조와 성분이동 등의 거동을 고찰하였다. CLC-G/CLC와 CLC/YSZ계면에서의 CLC면은 반응온도에 상관없이 XRD 관찰에서 주상은 La1-x CaxCrO3그리고 CLC와 반응하지 않은 YSZ면의 결정 상은 cubic-ZrO2으로 각각 나타났다. CLC/YSZ반응 계면의 성분이동은 Zr > La>>Cr>>>Ca 순이었으며, 온도에 따른 개개 성분의 이동도 차이는 크지 않았다. CLC/YSZ계면간의 결합은 계면성분간의 과다한 성분이동 없이 현 연구의 온도전체에 걸쳐 가능한 것으로 나타났다. CLC-G/CLC간의 SEM미세구조는 결합 면을 경계로 저온에서는 결정의 입자크기 차이를 보이다가 온도가 증가할수록 균일화되는 경향을 보였다.였다. 보였다.였다.

고상반응법과 sol-gel법으로 제조된 NASICON의 상온과 250˚C에서의 X선 회절 데이터를 리트벨트 분석을 행하였다. monoclinic에서 rhombohedral로 상전이가 일어나도 원자들의 변위는 매우 작았다. 이들 상간의 ZrO6 팔면체와 Si(P)O4 사면체고 구성된 골격은 다소 다르게 나타남으로 인하여 Na 이온의 자리도 변하였다. 이들 방법으로 제조된 NASICON은 Zr이 부족한 비화학양론 화학식, Na 1+x+4yZr2-xSixP3-xO12으로 표현될 수 있었다. 제조법에 따라 Na 이온들의 자리 점유율이 변화하였다. 상온에서는 Na(1)과 Na(3)자리의 자리 점유율의 합이 거의 1에 가까웠으나, 250˚C에서는 Na(1)과 mid Na 자리를 단위 화학식 당 한 개를 약간 상회하는 Na 이온이 점유하였다. 상온과 250˚C에서의 Na 이온의 이동 경로가 다름을 알 수 있었다. 또한 250˚C에서는 Na(1)자리와 Na(2)자리 사이에 mid Na가 존재하며, 이 자리가 Na 이온의 이동에 중요한 역할을 함을 알 수 있었다.