The objective of the present study is to investigate the increase in the functional characteristics of a substrate by the formation of a thin coating layer. Thin coating layers of have high potential because exhibits high hardness. Shock induced reaction synthesis is an attractive fabrication technique to synthesize uniform coating layer by controlling the shock wave. Ti and Si powders to form using shock induced reaction synthesis, were mixed using high-energy ball mill into small scale. The positive effect of this technique is highly functional coating layer on the substrate due to ultra fine substructure, which improves the bonding strength. These materials are in great demand as heat resisting, structural and corrosion resistant materials. Thin coating layer was successfully recovered and showed high Vickers' hardness (Hv=1183). Characterization studies on microstructure revealed a fairly uniform distribution of powders with good interfacial integrity between the powders and the substrate.

방향족 폴리아미드 역삼투 복합 박막에 트리알콕시알킬 실란 화합물을 안정적으로 정착시켜 내염소성이 향상된 복합막을 제조하는 방법에 관하여 조사하였다. 실란 화합물의 알킬 그룹의 탄소가 1개인 methyltriethoxysilane (METES)와 8개인 octyltriethoxysilane (OCTES) 표면 개질에 사용하였다. 긴 알킬 체인을 갖는 실란(OCTES)이 정착된 멤브레인의 경우, 일반 폴리아미드 역삼투막 또는 짧은 알킬 체인을 갖는 실란(METES)에 비해 개염소성이 크게 향상됨을 알 수 있었다. 본 연구에서는 표면 분석을 통하여 OCTES 코팅막과 METES또는 상용막과의 내염소성 차이를 설명하고자 하였다. EDX 원소 분석을 통하여 실란 화합물 둘 다 폴리아미드상에 안정적으로 고정되었음을 볼 수 있었으나 표면 조도나 접촉각 분석에서는 긴 알킬 체인을 가진 OCTES가 혐수성에 큰 영향을 주고 있음을 확인할 수 있었다.