Methanol was directly produced by the partial oxidation of methane with four-component mixed oxide catalysts. Four-component(Mo-Bi-Cr-Si) mixed oxide catalysts were prepared by the co-precipitation and sol-gel methods. The catalyst prepared by the sol-gel method showed about eleven times higher surface area than that prepared by the co-precipitation method. From the O2-TPD experiment of the prepared catalysts, it was proven that there exists two types of oxygen species, and the oxygen species that participates in the partial oxidation reaction is the lattice oxygen desorbing around 750℃. The optimum reaction condition for methanol production was 420°C, 50 bar, flow rate of 115 mL/min, and CH4/O2 ratio of 10/1.5, providing methane conversion and methanol selectivity of 3.2 and 26.7%, respectively.

페롭스카이트 촉매와 Mo, Bi를 기본으로 하는 복합 산화물 촉매를 이용하여 천연가스의 주성분인 메탄의 부분산화를 통하여 메탄올을 직접 합성하였다. 페롭스카이트(ABO₃) 촉매는 A 및 B site 성분을 변화시키면서 사과산법으로 제조하였으며, Mo, Bi를 기본으로 하는 3성분계 복합 산화물 촉매는 공침법으로 제조하여 반응특성을 살펴보았다. 페롭스카이트 촉매에서 A site에 알칼리 금속인 Sr을, B site에 전이금속인 Cr을 도입한 SrCrO₃ 촉매가 400℃에서 메탄올 선택도 11%로 가장 우수한 결과를 보였다. Mo, Bi를 기본으로 하는 3성분계 복합 산화물 촉매의 경우 모든 촉매에서 메탄 전환율에는 큰 차이를 보이지 않았으며, Cr을 첨가한 Mo-Bi-Cr 복합 산화물 촉매가 400℃에서 메탄올 선택도 15.3% 로 가장 우수한 결과를 나타냈다. 3성분계 복합 산화물 촉매에서 촉매의 활성과 메탄올 선택도는 촉매의 표면적에 정비례하였다.