In this paper, the experimental study and finite elements analysis were conducted on homogeneous and dissimilar metals single lap-shear bonded joints to investigate the factor that affect the joint failure load. It was found that factors which have the significant effects on the failure load of the joint was stiffness of the adherends. And from experimental results, it can be confirmed that the failure load increases linearly with overlap length increases. And the failure load of dissimilar metal joints is approximately 1KN(10 ～17%) larger than homogeneous metal joints. In order to confirm this phenomenon, the stress distribution and strain distribution of the specimens were analyzed through the finite element analysis. The difference between homogeneous metals joints and dissimilar metals joints is that stress and strain in adhesive are concentrated at the end of the overlap zone close to aluminium which has lower rigidity than aluminium in case of dissimilar metals joints. From high rigidity of steel, the stress concentration in bonds are decreased and it cause increase of the failure strength at dissimilar metal joints.

이종재 마찰용접재 강도특성과 초음파 반사계수와의 상관성에 관하여 실험적으로 연구한 결과의 요약은 다음과 같다. 1. 이종재 마찰용접 이음면에서의 초음파 반사계수를 펄스반사법에 의하여 측정산출할 수 있다. 2. 5MHz의 비교적 낮은 주파수의 탐촉자를 사용하므로써 시험편의 표면가공 오차를 무시할 수 있다. 3. 알루미늄과 스테인레스의 마찰용접에서는 용접조건으로 마찰가열시간이나 가열압력을 변수로 하였을 때보다 업셋가압력을 변수로 하였을 때 반사계수의 변화가 뚜렷하다. 4. 업셋가압력을 변수로 한 용접조건과 반사계수사이에는 선형적 상관관계가 있다. 5. 용접이음면에서의 이음인장강도와 반사계수와의 상관관계식을 정량적으로 도출할 수 있다. 6. 초음파 반사계수에 의해 이종재 마찰용접 품질의 비파괴적 평가가 가능하다