Delamination crack detection is very important for improving the structural reliability of laminated composite structures. This requires real-time delamination detection technologies. For composite laminates that are reinforced with carbon fiber, an electrical potential method uses carbon fiber for reinforcements and sensors at the same time. The use of carbon fiber for sensors does not need to consider the strength reduction of smart structures induced by imbedding sensors into the structures. With carbon fiber reinforced (CF/) epoxy matrix composites, it had been proved that the delamination crack was detected experimentally. In the present study, therefore, similar experiments were conducted to prove the applicability of the method for delamination crack detection of CF/polyetherethereketone matrix composite laminates. Mode I and mode II delamination tests with artificial cracks were conducted, and three point bending tests without artificial cracks were conducted. This study experimentally proves the applicability of the method for detection of delamination cracks. CF/polyetherethereketone material has strong electric resistance anisotropy. For CF/polyetherethereketone matrix composites, a carbon fiber network is constructed, and the network is broken by propagation of delamination cracks. This causes a change in the electric resistance of CF/polyetherethereketone matrix composites. Using three point bending specimens, delamination cracks generated without artificial initial cracks is proved to be detectable using the electric potential method: This method successfully detected delamination cracks.

하전된 멤브레인 미세기공으로 유체가 흐르는 경우는 계면동전기 효과가 작용하게 된다. 비선형 Poisson-Boltzmann 전기장과 흐름에 의해 유발되는 전기장 사이의 정전상호작용을 운동방정식의 외부작용 힘으로 고려하였다. 유한차분법으로 정전위 분포를 우선 산출하고, 이어서 Green 함수로 슬릿형 기공에 대한 Navier-Stokes 식의 해석해를 구하였다. 계면동전기적 유동에 의한 흐름전위를 관련된 물리화학적 인자들의 함수로 유도되는 해석적인 명확한 표현으로 제시하였다. 전기이중층, 표면전위, 그리고 기공벽면의 하전조건의 영향에 따른 유속분포와 흐름전위 변화를 고찰하였다 계산결과, 전기이중층 두께나 표면전위가 증가함에 따라 평균유속은 감소하는 반면에 흐름전위는 증가하였다.

In the removal of heavy metals from the mine deposit using electrokinetic processes, the effects of operation under both constant current and constant potential conditions were estimated. The results of soil pH distributions for DDW-20 V and DDW-100 ㎃ cases after the electrokinetic remediation tests were observed. In the former case, soil pH was not much changed and kept to almost constant value just little higher than initial soil pH of 3.52, except near the cathode, which was about pH 5. While in the latter case, soil pHs of anode and the cathode regions were less than pH 3 and about 6, respectively. The electroosmotic flow to the cathode increased rapidly till 10 hrs and decreased steadily and then maintained to constant rate until the end of operation at constant current condition. Electric potential gradient was continuously increased to as much as 34.375 V/cm. At the steady state, values of the apparent electric conductivity for DDW-20 V and DDW-100 ㎃ were around 40 ㎲/㎝ and 30 ㎲/㎝, respectively. In the DDW-100㎃ test, Cu, Cd, and Zn except Pb showed the tendency of moving toward the cathode. While in the DDW-20 V case, it was observed that Cu, Zn, and Pb except Cd were not moved to any directions. The results of the tests demonstrated that the electrokinetic soil remediation process could be operated better under constant current condition than constant electric potential condition.