PURPOSES : In this study, experimental findings regarding the frost resistance of concrete incorporated with mineral admixtures such as fly ash (FA) and ground granulated blast-furnace slag (SG) are presented. METHODS : To evaluate the performance of the abovementioned concretes under repeated freezing and thawing environments, based on the ASTM C 666 standard, the relative dynamic modulus of elasticity and mass ratio measurements are performed regularly. Furthermore, based on the ASTM C 672 standard, the concretes are exposed to 4% CaCl2 and NaCl salt solutions along with repeated 50 cycles of freezing and thawing. Subsequently, the scaling resistance is evaluated based on the scaled-off mass content and visual examination. RESULTS : SG is less effective in enhancing the scaling resistance of concrete compared with FA. However, the concrete incorporated with SG is more resistant to repeated freeze-thaw actions compared with OPC concrete. Meanwhile, compared with OPC concrete, the concrete incorporated with FA indicates a similar performance in terms of scaling resistance and better resistance against repeated freeze-thaw actions. CONCLUSIONS : The frost resistance of concrete depends significantly on the types of mineral admixtures used in concrete. This emphasizes the importance of selecting the appropriate binder to achieve durable concrete pavements in cold climate regions.

본 연구에서는 염화물이 함유된 동결수에 의한 콘크리트의 내동해성을 검토하기 위하여 동결융해 및 표면스케일링 저항성을 평가하고자 하였으며, 이를 위한 배합으로서 물결합재비는 0.37, 0.42, 0.47의 3수준, 결합재 방식은 일반 OPC 콘크리트, 고로슬래그 미분말 50%의 2성분계 콘크리트 및 플라이애시 15%와 고로슬래그 미분말 35%의 3성분계 콘크리트로 설정하였다. 그 결과, 고로슬래그 미분말 50% 및 플라이애시 15%와 고로슬래그 미분말 35%의 혼합 시멘트계 콘크리트의 경우 일반 OPC 콘크리트에 비하여 동결융해 및 표면스케일링 저항성이 상대적으로 우수하게 나타났으며, 이를 통해 내구성 저하가 우려되는 해양 환경 하에서 비래염분 및 비말 등의 해수의 작용에 의한 콘크리트의 내구성 저하현상을 억제하기 위한 방안으로서 슬래그의 활용이 유효함을 확인할 수 있었다.