Coke aggregates and carbon artifacts were produced to investigate the interactions of coke and pitch during the kneading process. In addition, the kneading ratio of the coke and binder pitch for the coke aggregates was controlled to identify the formation of voids and pores during carbonization at 900°C. Experiments and thermogravimetric analysis revealed that carbon yields were improved over the theoretical yield calculated by the weight loss of the coke and binder pitch; the improvement was due to the binding interactions between the coke particles and binder pitch by the kneading process. The true, apparent, and bulk densities fluctuated according to the kneading ratio. This study confirmed that an excessive or insufficient kneading ratio decreases the density with degradation of the packing characteristics. The porosity analysis indicated that formation of voids and pores by the binder pitch increased the porosity after carbonization. Image analysis confirmed that the kneading ratio affected the formation of the coke domains and the voids and pores, which revealed the relations among the carbon yields, density, and porosity.

본 연구는 남녀 대학생을 대상으로 동일색조 코디네이션과 1:2:3면적비 변화에 따른 스트라이프 넥타이의 감성이미지와 상호작용효과를 알아보고자 한다. 이들 단서로 사용된 56개 자극물은 4가지 색조합, 2가지 색조, 7가지 면적비로 구성되었고, 감성이미지는 26개의 형용사쌍에 대해 7단계로 평가되었다. 조사대상자는 경남, 서울, 부산, 대구 등지에 거주하는 대학생 1344명의 피험자로 하였으며, 그 연구결과는 다음과 같다. 동일색조 코디네이션과 1:2:3면적비 변화에 따른 스트라이프 넥타이의 감성이미지를 요인분석한 결과 매력성, 젊음 활동성, 현시성, 능력성, 온유성의 5가지 차원으로 도출되었다. 색조합과 색조는 감성이미지의 모든 요인에서 독립적인 영향을 나타내었다. 또한 색조는 면적비와 상호작용하여 현시성과 능력성 요인에서 두드러진 단서로 작용하였다. 성별과 면적비는 젊음 활동성 요인에서, 성별과 색조는 온유성 요인에서, 색조합과 색조는 현시성과 온유성 요인에서 상호작용효과를 나타내었다. 이러한 연구결과는 남성 코디네이션을 위한 효과적인 기초자료로 활용될 것이다.