In this work, uniform and nanosize(75nm) silicalite-1 crystals was hydrothermally synthesized by using 9TPAOH:0.16NaOH:25Si:495H2O solution at 80 ℃. They were applied as seed in the secondary growth process for preparing silicalite-1 membrane by template-free method. The highest ethanol/water separation factor of 119 with flux 0.58kg/m². Furthermore, these membranes (nano seed, template free silicalite-1 membrane) exhibit high permselectivity of He over SF6(123), and small gas permeation mechanism and Knudsen diffusion studies suggest that the membranes contain negligible intercrystalline or non-zeolite pores.

In this work, uniform and nanosize(75nm) silicalite-1 crystals was hydrothermally synthesized by using 9TPAOH:0.16NaOH:25Si:495H2O solution at 80 ℃. They were applied as seed in the secondary growth process for preparing silicalite-1 membrane by template-free method. And silicalite-1 membrane, which was coated by nano-size seed, showed a high EtOH/H2O separation factor of 128. The high separation factor could be explained by the role of nanosize seed. The application of nanosize seed successfully retarded the formation of interfacial voids between silicalite-1 grains. Therefore, it could be concluded that template-free hydrothermal process can produce silicalite-1 membrane with well performance.

양극산화 알루미나(AAO)막의 나노 사이즈 미세공(세공 크기 20 nm, 10 nm 및 200 nm)을 주형으로 사용하여 전도성 고분자인 폴리피롤, 폴리아닐린 중합체 및 폴리피롤/폴리아닐린 공중합체 나노와이어를 제조하였다. 미세공 주형 내에서 전도성 고분자의 성장은 세공의 벽면을 따라 튜브 형태로서 성장하였으며, 3시간 이후에는 내부가 완전히 채워진 나노와이어가 형성되었다. AAO 막을 수산화나트륨 용액으로 퍼리하여 세공 내에 형성된 전도성 고분자 나노와이어를 회수 하였으며. 회수된 나노와이어 직경과 길이는 주형 막의 세공 형상과 일치하였다. 통상의 용액 중합법으로 제조된 전도성 고분자 분말과 비교하여 주형 합성법으로 제조된 전도성 고분자 나노와이어는 결정성과 열적 안정성이 향상되었으며, 전기 저항은 4~60% 감소하였다.