The untreated effluent dropping into the environment from various textile industries is a major issue. To solve this problem, development of an efficient catalyst for the degradation of macro dye molecules has attracted extensive attention. This work is mainly focused on the synthesis of nickel–manganese sulfide decorated with rGO nanocomposite (Ni–Mn-S/rGO) as an effective visible photocatalyst for degradation of textile toxic macro molecule dye. A simple hydrothermal method was used to synthesize Ni–Mn-S wrapped with rGO. The prepared composites were characterized using various techniques such as X-ray diffraction (XRD), high-resolution scanning electron microscopy (HR-SEM), high-resolution transmission electron microscopy (HR-TEM), Fourier transform infra-red spectrometer (FTIR), and ultra violet–visible (UV–Vis) spectroscopy. The photocatalytic performance of nickel sulfide (NiS), manganese sulfide (MnS), nickel–manganese sulfide (Ni–Mn-S), and Ni–Mn-S/rGO nanocomposite was assessed by analyzing the removal of acid yellow (AY) and rose bengal (RB) dyes under natural sun light. Among these, the Ni–Mn-S/rGO nanocomposite showed the high photocatalytic degradation efficiency of AY and RB dyes (20 ppm concentration) with efficiency at 96.1 and 93.2%, respectively, within 150-min natural sunlight irradiation. The stability of photocatalyst was confirmed by cycle test; it showed stable degradation efficiency even after five cycles. This work confirms that it is an efficient approach for the dye degradation of textile dyes using sulfide-based Ni–Mn-S/rGO nanocomposite.

How to effectively deal with the polluted water by the pollutant of organic dyes is the world problem. It is of great significance if the organic dyes in the polluted water can be directly turned into the useful materials through a facile approach. Herein, the water which contains the common organic dye, Reactive red 2 (RR2), has been chosen to be the model to synthesize graphene quantum dots (GQDs) by a facile route. The comprehensive characterizations, including TEM (HRTEM), XPS, Raman, PL and UV–Vis. spectra, have been performed to confirm the structures and explore the properties of the synthesized GQDs. Meanwhile, the excellent PL properties and low biotoxicity of the GQDs confer them with the potential applications in the biological fields. When the GQDs are excited by the wavelength of 360 nm, the maximum emission is achieved at 428 nm. It is well demonstrated that the synthesized GQDs are able to detect the Al3+ which causes multiple diseases, such as Parkinson, Alzheimer, kidney disease, and even cancer. The detection range is from 90 to 800 μM, which is different from the reported kinds of the literature. Therefore, this work not only provides an economical and environmental route on solving the universal problem from organic dyes, but also facilitates to advancing the synthesis and application of GQDs.

염료감응형 태양전지에 사용되기 위한 유기/무기 복합소재를 합성하였다. 다양한 분자량(400, 600, 1,500, 3,400)의 polyethylene glycol의 양 끝단을 ethoxysilane기로 치환하여 전구체를 제조하였으며, 전구체의 졸-겔 반응을 통하여 복합소재를 합성하였다. 전해질막은 유기/무기 복합소재를 NaI 및 I2로 도핑하여 제조하였으며, 제조한 전해질막의 이온전도 특성을 측정하였다. 전해질막의 이온전도도는 원료로 사용한 PEG에 크게 영향을 받았으며 가장 높은 이온전도도는 분자량 1,500의 PEG를 원료로 사용한 전해질 막에서 볼 수 있었다. 복합전해질막은 전도도에 있어서 큰 향상을 보였다. PEO 전해질막에 비하여 분자량 1,500의 PEC로 제조한 복합전해질막은 월등하게 높은 이온전도도를 보였다.