Chitosan powder is synthesized by a deasetylation process of chitin, obtained from processing of dried shrimp shell powder. Subsequently, chitosan (CS) membranes filled by montmorillonite (MMT) particles and phosphotungstic acid are prepared, and characterized by FT-IR and SEM. The morphology, obtained by SEM for the composite membrane, showed that MMT filler is successfully incorporated and relatively well dispersed in the chitosan polymer matrix. Water and methanol uptake for the CS/MMT composite membranes decrease with increasing MMT loadings, but IEC value increases. In all prepared CS/ MMT composite membranes, the CS membrane filled by 5 wt% MMT particles exhibits the best proton conductivity, while that with 10 wt% MMT loading exhibits the lowest methanol permeability; these values are 2.67 mS·cm−1 and 3.40 × 10−7 cm2·s−1, respectively. The best membrane selectivity is shown in the CS/MMT10 composite membrane; this shows that 10 wt% filled MMT is the optimum loading to improve the performance of the chitosan composite membrane. These characteristics make the developed chitosan composite membranes a promising electrolyte for direct methanol fuel cell (DMFC) application.

폴리스티렌-블록-폴리히드록에틸 메타크릴레이트(PS-b-PHEMA), 술포석시닉산(SA), 인텅스텐산(PWA)으로 구성된 수소 이온 전도성 나노복합 고분자 전해질막을 제조하였다. 폴리히드록에틸 메타크릴레이트(PHEMA) 블록의 히드록실그룹(-OH)와 술포석시닉산(SA)의 -COOH 그룹과의 에스테르 반응에 의하여 전해질막을 가교시켰다. 폴리헤테로산(PWA)을 도입했을 때, SO3 - 그룹의 신축 밴드가 1187 cm -1에서 1158 cm -1로 낮아졌으며, 이는 PWA 입자가 전해질막의 술폰산 그룹과 상호작용함을 나타낸다. PWA 함량이 30wt%가 되었을 때, 상온 전도도는 0.045에서 0.062S/cm로 증가되었으며, 이는 PWA 입자의 고유 전도도 특성과 전해질막의 술폰산기의 산도가 증가했기 때문이다. 또한 30wt%를 함유한 복합 전해질막은 100℃에서는 최대 0.126 S/cm의 수소 이온 전도도를 나타내었다 PWA가 첨가됨에 따라 복합 전해질막의 열적특성 또한 증가하였다.