Perfluorinated sulfonic acid (PFSA) ionomers have been widely used for renewable energy generation, including polymer electrolyte fuel cells (PEFCs), owing to their excellent resistance to harsh chemicals and good ion-transport properties. PFSA materials experience critical chemical decomposition to radical attacks, and fast hydrogen crossover leading to fairly reduced electrochemical performances, when they are used as membrane materials. Similar chemical degradation also occurs in PEFC electrodes containing PFSA ionomer binders used as both mechanical supporters and proton conductors and shortens PEFC lifetime. In this study, several approaches based on their morphological rearrangement to overcome these economical and technical issues are proposed. They include pore-filling membrane formation, nanodispersion, and their combination.

친전자성 치환반응을 통하여 제조된 술폰화 단량체와 비(非)술폰화 단량체의 직접 중합법을 통하여 서로 다른 술폰화도를 나타내는 술폰화 폴리아릴에테르술폰 공중합체를 합성하고, 이들로부터 직접 메탄올 연료전지용 이중층(層) 고분자 전해질 막을 제조하였다. 우수한 이온 전도특성을 나타내는 술폰화도 50%의 공중합체를 사용하여 전해질 막의 모체(母體) 전도층을 제조하고, 이들의 한쪽 표면에 술폰화도 10%의 공중합체를 도포한 후 건조하여 낮은 메탄올 투과 특성의 코팅층을 형성시켰다. 도포되는 공중합체의 질량비를 5~20%로 조절함으로써 코팅 층 두께에 따른 전해질 막의 특성 변화를 고찰하였으며, 형성된 코팅 층을 막-전극 접합체의 음극 면에 접합시켜 운전 시 메탄올 연료와 직접 접촉하도록 하였다. 이중층 형성 공정을 통하여, 단일 전해질 막과 동등한 수준의 이온 전도 특성을 유지하면서도, 전해질 막을 통한 메탄올 투과 특성이 현저히 개선된 우수한 효율의 고분자 전해질 막 제조가 가능하였다. 작동 온도 60°C, 2 M의 메탄올 공급 환경에서 수행된 연료 전지 성능 평가 결과, 막-전극 접합체 출력 밀도는 5%의 질량비에서 최대 134.01 mW/cm2였으며, 이로부터 상용 나피온 115 대비 105.5%의 향상된 성능 효율을 확인할 수 있었다.