Synthesis of composite powders for the Fe2O3-Zn system by mechanical alloying (MA) has been investigated at room temperature. Optimal milling and heat treatment conditions to obtain soft magnetic composite with fine microstructure were investigated by X-ray diffraction, differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM) measurement. It is found that α-Fe/ZnO composite powders in which ZnO is dispersed in α-Fe matrix can be obtained by MA of Fe2O3 with Zn for 4 hours. The change in magnetization and coercivity also reflects the details of the solid-state reduction process of hematite by pure metal of Zn during MA. Densification of the MA powders was performed in a spark plasma sintering (SPS) machine at 900 ~ 1,000 ℃ under 60 MPa. Shrinkage change after SPS of sample MA'ed for 5 hrs was significant above 300 ℃ and gradually increased with increasing temperature up to 800 ℃. X-ray diffraction results show that the average grain size of α-Fe in the α-Fe/ZnO composite sintered at 900 ℃ is in the range of 110 nm.
Fabrication of soft magnetic composite powders for the Fe2O3-Ca system by mechanical alloying(MA) has been investigated at room temperature. It is found that soft magnetic composite powders in which CaO is dispersed in α-Fe matrix are obtained by MA of Fe2O3 with Ca for 5 hours. Changes in magnetization and coercivity also reflect the details of the solidstate reduction process of hematite by pure metal of Ca during MA. The saturation magnetization of MA powders increases with increasing MA time and reaches a maximum value of 65 emu/g after 7 hours of MA. The average grain size of α-Fe in MA powders, estimated by diffraction line-width, gradually decreases with increasing MA time and reaches 52 nm after 5 hours of MA. It can also be seen that the coercivity of the 5-hour MA sample is fairly high at 190 Oe, suggesting that the grain refinement of already-produced α-Fe tends to clearly occur during MA.