This study investigated the effect of solvent on the fabrication of Ni-free Fe-based alloy nano powders by employing the PWE (pulsed wire evaporation) in liquid and compared the alloy particles fabricated by three different methods (PWE in liquid, PWE in Ar, plasma arc discharge), for high temperature oxidation-resistant metallic porous body for high temperature soot filter system. Three different solvents (ethanol, acetone, distilled water) of liquid were adapted in PWE in liquid process, while X-ray diffraction (XRD), field emission scanning microscope (FE-SEM), and transmission electron microscope (TEM) were used to investigate the characteristics of the Fe-Cr-Al nano powders. The alloy powder synthesized by PWE in ethanol has good particle size and no surface oxidation compared to that of distilled water. Since the Fe-based alloy powders, which were fabricated by PWE in Ar and PAD process, showed surface oxidation by TEM analysis, the PWE in ethanol is the best way to fabricate Fe-based alloy nano powder.

Eu3+ doped YGdO3 phosphors particles which have fine size and narrow size distribution with non aggregated uniform morphology were prepared by solvent evaporation method for the improvement of emission efficiency. Several parameters have been investigated in this study such as the influences of composition ratio of host materials, calcination temperature, amount of activator, surfactant, pH and flux on the photoluminescence intensity, particle size and dispersion. Eu3+ doped YGdO3 phosphor presented a strong narrow band emission peak at 612nm. The maximum emission intensity ofYGdO3:Eu3+ occurred when Eu3+ concentration is 3wt% under vacuum ultra violet excitation. Prepared phosphors were found to have small round-shaped particles about 150nm in size. The addition of PVA as a surfactant inhibits the grain growth and the agglomeration of particles efficiently by reducing the oxygen bridge bonds. As the pH reduces, PL intensity increase due to reducing the formation of oxygen bridge bonds. The particles prepared from solvent evaporation method with 5wt% LiCl were found to have 120% PL intensity compare to particles prepared without LiCl flux.