The bead geometry according to the welding conditions was analyzed through the laser fillet welding experiment of 9% Ni steel, and the relationship between the shear strength and the five bead geometry measured by selecting the main bead geometry of the fillet weld was analyzed. Among the welding conditions, the welding conditions that directly affect the penetration depth are welding speed and laser power, and the working angle and beam position have a great influence on the formation of leg of vertical and horizontal members. The bead shape, which greatly affects the shear strength, is the horizontal member length, neck thickness, and weld length, and has a proportional relationship with the shear strength. As a result of confirming the relationship between shear strength and bead shape through the derivation of the trend line, it was confirmed that the length of the vertical member, whose R2 value was 0.92, was most closely related to the shear strength.

P92 steel weldment scheduled to use for next generation ultra super critical(USC) boiler header is assessed on creep characteristics. The test method to assess local structure of weldment is small-punch creep(SP-Creep) test, which is a kind of micro test proved the availability on evaluation of mechanical property for local structure. The results for P92 steel weldment are compared with that of tensile creep test for same microstructures of steel weldment. Overall, the creep resistance of coarse grain HAZ(CGHAZ) at 650℃ is inferior to the other structures while fine grain HAZ(FGHAZ) is most superior in the P92 steel weldment. The power law relationships can be obtained for each weldment structures(BM, ICHAZ, FGHAZ, CGHAZ and W.M) of USC boiler header

1.0Cr-1.0Mo-0.25V강 용접부의 크립 파단 시험시 파단 발생 원인에 관한 연구가 시행되었다. 파괴는 Intercritical Heat Affected Zone에서 발생하였으며 파단면에서 구상의조대한 M6C탄화물이 발견되었다. 모재는 molybdenum 주성분의 M2C, vanadium 주성분의 M4C3 및 chromium 주성분의 M23C6와 M7C3 탄화물이 존재하였다. 모의 실험 결과 준안정 상태인 M2C 탄화물은 850˚C, 10oh에서 안정한 M6C탄화물로 변태하였다. M6C 탄화물은 주변의 molybdenum 농도를 떨어뜨려 강도의 저하를 가져오며 크립 기공의 발생 원인을 제공하였다.