The effects of Nb and Cr addition on the microstructure, corrosion and oxide characteristics of Zr based alloys wereinvestigated. The corrosion tests were performed in a pressurized water reactor simulated-loop system at 360oC. Themicrostructures were examined using OM and TEM, and the oxide properties were characterized by low-angle X-ray diffractionand TEM. The corrosion test results up to 360 days revealed that the corrosion rates were considerably affected by Cr contentbut not Nb content. The corrosion resistance of the Zr-xNb-0.1Sn-yCr quaternary alloys was improved by an increasing Nb/Cr ratio. The crystal structure of the precipitates was affected by a variation of the Nb/Cr ratio. The Zr-Nb beta-enrichedprecipitates were mainly formed in the high Nb/Cr ratio alloy while Zr(NbCr)2 precipitates were frequently observed in the lowNb/Cr ratio alloy. The studies of oxide characteristics revealed that the corrosion resistance was related to the crystal structureof the precipitate.

2원계 (Zr-xNb, Zr-xSnl 와 3원계 (Zr-O.8Sn-xNb, Zr-O.4Nb-xSnl Zr합금의 기계적 특성에 미치는 Nb와 Sn의 영향올 조사하기 위하여 인장시험 빛 마세조직 분석을 실시하였다. Nb와 Sn량이 많이 첨가될수록 2원계와 3원계 합금의 강도는 정진적으로 증가하는 경향을 보이는데, Nb와 Sn이 고용도 이상으로 첨가될 때 강도중가는 더욱 두드러진 것으로 냐타났다. 강도 증가현상을 고용강화, 석출강화, 결정립 미세화에 의한 강화, 집합조직에 의한 강화효과 관정에서 분석한 결과, 고용강화 효과가 가장 두드러지며 Nb와 Sn이 고용도 이상에서는 석출강화가 강도에 기여하는 것으로 냐타났다. 합금원소 첨가에 따른 결정립미세화도 강도에 약간은 영향을 미치는 것으로 사료된다. 그러나 집합조직은 합금원소 변화에 따라서 거의 변화가 없는 것으로 냐타났으므로 집합조직은 강도증가에 기여하지 않는 것으로 생각된다.