CSA, a cement mineral compound that is mainly composed of 3CaO·3Al2O3·CaSO4, generates ettringite as a hydration product after a reaction with glass (lime), gypsum and water to speed up the hardening process and enhance the strength and degree of expansion. When used as a cement admixture, there is increased production of ettringite, which can improve the initial strength in the first three days and ameliorate the reduction in the initial strength caused by the use of fly ash in particular. In this study, a hydrate analysis was performed using XRD and SEM after substitution with fly ash (30%) and CSA (8%) with the goal of observing the effect of CSA on the initial strength of a cement mixture containing fly ash. The results of the analysis showed that an addition of CSA promoted the production of ettringite and improved the initial strength, resulting in the generation of hydrates, which can effectively enhance the long-term strength of these materials.

온도 및 수분 등과 같은 환경적인 요인들은 슬래브의 컬링을 유발하여 줄눈 콘크리트 포장의 장기적인 거동과 공용성에 영향을 미치는 것으로 알려져 있다. 하지만, 콘크리트 슬래브의 컬링에 관한 상세한 조사가 부족한 실정이므로 컬링과 이에 미치는 요인들의 관계는 아직까지도 명확하게 정의되지 못하고 있다. 본 연구에서는 현장에 건설된 줄눈 콘크리트포장의한 슬래브에 각종 계측기를 매설하여 콘크리트 슬래브의 온도, 상대습도, 변형률, 연직변위, 그리고 슬래브 좌우측 줄눈부의 수평방향 움직임을 조사하였다. 콘크리트 타설 직후부터 약 4일간 측정된 현장자료를 분석하여 초기 재령 콘크리트 슬래브의 컬링에 미치는 온도 및 수분의 영향과 줄눈강성의 크기에 따라 컬링이 구속되는 정도를 조사하였다. 콘크리트 슬래브의 컬링은 주로 온도의 영향 때문에 24시간주기의 사이클을 나타내었으며. 장기적인 건조수축의 영향으로 상향의 컬링이 점차 증가하는 경향을 보였다. 또한, 컬링의 크기와 변화량이 골재 맞물림 등에 기인하는 줄눈강성에 영향을 크게 받는 것으로 조사되었다. 향후 온도에 의 한 계절별 줄눈강성의 변화와 장기적인 건조수축이 콘크리트 슬래브의 컬링에 미치는 영향을 추가로 조사할 예정이다.

연속철근콘크리트포장에서 횡방향 균열은 초기의 온도와 습도변화로 인해 발생하며 횡 방향 균열의 폭과 간격은 하중전달효율 및 펀치아웃과 같은 포장공용성에 직접 관련된다. 또한, 연속철근콘크리트포장에서 균열폭은 콘크리트의 건조수축 뿐만아니라 소위 특성 온도변화 시점으로 정의되는 "제로-스트레스 온도"에 의존한다. 연속철근콘크리트포장의 양호한 장기공용성을 위해서 횡방향 균열은 매우 작은 폭으로 유지될 필요가 있으며 초기재령 에서 온도제어는 이를 위한 필수요소라 할 수 있다. 따라서, 본 연구에서는 페이브프로를 사용하여 콘크리트 온도를 예측하였으며 현장실험을 통한 실측온도와 비교하고 균열조사를 수행하였다. 본 연구로부터 도출된 결과는 첫째, 실측온도는 0.2~4.5℃의 범위에서 예측온도보다 큰 것으로 나타났으며 정확한 콘크리트 온도예측을 위해서는 수화특성치로 고려되는 활성화 에너지와 단열온도상수가 입력변수에서 정확히 고려되어야 할 것으로 판단되었다. 둘째. 콘크리트 타설 후 24시간 이내의 온도는 오후에 비하여 오전에 타설된 콘크리트에서 더 크게 나타났으며 최대온도는 정오에 타설된 온도에서 발생되었다. 마지막으로 재령 12일에 조사된 균열발생률은 오전에 타설된 구간에서 25% 증가되고 그 만큼 균열간격은 감소하는 것으로 나타났다. 이 결과로부터 최대 콘크리트 온도는 균열발생에 크게 영향을 미치며 콘크리트 온도제어는 연속철근콘크리트포장의 양호한 공용성을 위해 필요할 것으로 판단되었다.

초기재령 콘크리트 수화과정의 메카니즘과 초기재령 콘크리트 균열 제어기법의 개발은 주로 매시브한 콘크리트를 대상으로 실험적 연구와 수치해석적 연구가 이루어져 왔으나 철근 콘크리트 라멘교의 상부슬래브와 같이 비교적 두께가 적은 부재에 대해서는 연구 내용이 거의 없는 실정이다. 본 연구에서는 4개의 철근 콘크리트 라멘교의 상부 슬래브에 대한 수화열을 현장 실측하여 온도이력과 강도 발현 모텔 및 건조수축 모델에 의한 응력들을 근거로 하여 초기 재령 철근 콘크리트 라멘교의 상부슬래브에 발생할 수 있는 균열을 제어할 수 있는 설계기법을 제시하였다. 본 연구의 해석기법을 이용하여 초기재령 철근 콘크리트 라멘교의 상부슬래브에 발생되는 균열 폭을 계산하여 균열제어를 위한 철근량 산정방법을 제시하였고, 설계하중 재하 시 배력철근으로만 취급되는 헌치부의 철근이 초기재령 철근콘크리트 라멘교의 온도응력 검토 시에는 주철근이 됨을 알 수 있었다. 제안한 해석기법은 초기재령 철근콘크리트 라멘교의 온도균열제어를 위한 설계에 적용될 수 있을 것으로 판단된다.

이 연구에서는 단일 활성화제로 활성화시킨 슬래그 기반 섬유보강 복합재료의 초기재령에서 인장거동을 조사하였다. 실험 결과, 활성화제 종류에 따라 재령 7일에서 균열강도, 인장강도, 인장변형성능에 차이가 있었으며, 규산나트륨을 활성화제로 사용한 배합이 가장 큰 인장변형성능을 나타내었다.

매립지 감소 및 천연 잔골재의 부족으로 인해 산업부산물을 콘크리트의 골재로 사용하려는 연구가 최근 들어 빠르게 진행되고 있다. 본 연구에서는 EOS 잔골재를 치환하여,OPC 콘크리트 배합과 GGBFS 배합을 대상으로 초기재령에서의 공학적 특성을 평가하였다. 실험은 EOS 잔골재를 0%, 30%, 50%로 치환, GGBFS를 0%, 40% 치환하여 물-결합재비 60% 콘크리트로 실험을 진행하였다. 굳지 않은 콘크리트에서 슬럼프, 공기량, 단위용적질량을 평가하였으며, 경화 콘크리트에서 압축강도와 NT BUILD 492 방법을 이용한 염화물 확산계수를 도출하고 EOS 골재 치환에 따른 내구성능을 평가하였다. 본 연구의 실험결과 EOS 잔골재를 치환함에 따라 재령 3일, 7일까지는 압축강도 발현이 각 기준 배합에 비해 증가함을 확인하였지만, 재령 28일에서는 일부 감소하는 것을 확인하였다. 또한 촉진 염화물 침투 실험결과, GGBFS 콘크리트 배합에서 OPC콘크리트 배합과 비교하여 약 60~67% 감소하였으며, EOS 잔골재 50% 치환 배합에서 가장 낮은 염화물 확산계수가 나타남에 따라 EOS 잔골재가 OPC 및 GGBFS 콘크리트에 사용될 수 있는 공학적 가능성을 제시하였다.

The concrete track has been developed as an alternative to the ballast track due to its excellent maintenance. Recently, QHT(Quick Hardening Track) has been developed to rapidly replace ballast track to slab track. In bridge section, post-installation anchors should be installed at the center of QHT segment in order to unify the behavior of bridge and QHT. In this study, track-bridge interaction analysis was performed to check safety of anchor considering at early age of QHT.

This paper presents the findings of the study conducted to evaluate workability and compressive strength characteristics of rapid-setting concrete containing metakaolin. The experimental variable selected was the rate of cement replacement with metakaolin at 0, 5, 10, and 15 percent. The findings are summarized as follows: compared with the control specimens with no replacement rate, the workability and compressive strength of the concrete with 5% of cement replaced with metakaolin were comparable to those of control specimens at 4hours; however, at 72 hours, the compressive strength of the concrete with the same replacement rate was larger than the strength of the control specimens by 4.1%, while no increase in strength was observed at higher replacement rates, implying that the optimum replacement rate of cement with metakaolin is 5%.

본 연구에서는 산업부산물인 TDFA를 혼입한 콘크리트에 대하여 초기재령의 공학적 특성을 분석하였다. 물-결합재비 0.5, FA 치환 율 20%인 콘크리트를 대상으로 TDFA를 3~12%치환하여 경화 전 및 경화 후의 특성을 분석하였다. TDFA 혼입율 6% 이후의 배합에서는 작업 성이 현저하게 감소하였고 공기량 확보가 어려웠으며, 이로 인해 감수제 및 공기연행제를 추가하여 작업성을 개선시켰다. TDFA 혼입율 6~12% 까지는 콘크리트의 강도에 큰 영향은 없었으며, 탄산화저항성 및 염해저항성에서는 FA 20% 치환 배합보다 우수한 성능을 나타내었다. 그러나 공기량이 부족한 TDFA 혼입율 6%배합에서는 동결융해 저항성이 크게 감소하였다. 공기량 및 작업성이 확보된다면 FA를 12%수준까지 TDFA로 치환해도 공학적인 성능을 확보할 수 있을 것으로 판단된다.

This paper describes the findings of the study conducted to evaluate early-age strength characteristics of rapid-setting concrete containing waste pottery powder. The experimental variables selected were 5, 10, and 15 percent replacements of cement with waste pottery powder. The findings are summarized as follows: (1) slump of the concrete decreased as the replacement rate of cement with waste pottery powder increased, and (2) compared with the strength of the control specimens with no replacement rate, compressive strength of concrete increased at 5% replacement rate, and was comparable to the control at 10% replacement rate; however, at 15% replacement rate, compressive strength actually decreased.

To evaluate the quality of the concrete cover a research project using non destructive air permeability measurements is carried out. Measurements were conducted in the laboratory as well as on concrete structures.

In This study to estimate the early-age strength of concrete, the electro-mechanical impedance method was utilized. The electro-mechanical impedance varies with the mechanical properties of host structures. Because the strength development is most influential factor among the change of mechanical properties at early-age of curing, it is possible to estimate the strength of concrete by analyzing the change of E/M impedance.

The possibility to determine the setting time of cement paste using the electrical impedance response of early-age hydrating cement paste is investigated. Electrical impedance responses of cement paste are continuously measured immediately after mixing and during hydration process. Measured responses are then analyzed and compared with temperature responses of hydrating cement paste.

To the goal of improving the early compressive strength of the mortar including Ground granulated blast furnace slag under low-temperature environment, Industrial byproducts including SiO2 and Al2O3 was fired and than 7% of it was added into Ground granulated blast furnace slag. By checking compressive strength and activity index from different mixing rate, in spite of low strength development than OPC 100%, when using firing powder, the expectation of increasing strength by curing time was affirmative

이 연구에서는 콘크리트 초기재령시의 역학적 특성을 분석하고 수화반응 및 발열반응으로 인한 콘크리트 내부에서 발생하는 온도 및 상대습도의 변화에 대한 분석을 실시하고자 하였다. 세 가지의 다른 단위시멘트량을 실험변수로 하였으며, 타설 직후부터 콘크리트 내부의 온도 및 상대습도의 변화 계측하기 위하여 새로운 계측시스템을 개발하였다. 단위시멘트량에 압축, 인장 및 휨강도의 변화는 크지 않았으며, 재령 7일 이후에는 증가가 많지 않았다. 각 측정부위별 최고 온도는 타설 후 약 11시간 정도 경과 시에 발생되었으며 이후 점차 온도가 낮아지다가 양생 1일 경과 후 거푸집 탈형 이후부터 온도가 하강하기 시작했다. 각 측정부위별, 온도감소 분석 결과, 콘크리트 구조물의 위치 및 노출조건에 따라 온도의 변화가 굉장히 다른 것으로 분석되었으며, 초기재령에서 콘크리트 내부의 상대습도의 변화는 수화반응에 영향을 미치는 단위시멘트량 보다는 외부에 노출된 상태가 더 큰 영향을 미칠 수 있는 것으로 분석되었다.

본 연구에서는 보통포틀랜드시멘트(OPC: ordinary Portland cement), 플라이애쉬(PFA: pulverised fly ash), 고로슬래그미분말(GGBFS: ground granulated blast furnace slag), 실리카퓸(SF: Silica fume)등의 각종 결합재를 적용한 시멘트 페이스트의 염소이온 고정화능력에 관하여 연구하였다. 각각의 사용 시멘트 페이스트는 40%의 물/결합재로 PFA, GGBFS 및 SF 혼화제의 각기 다른 치환률을 갖도록 하였으며 미리 혼합수내에 결합재 중량당 0.1～0.3%의 염소이온을 배합수내에 혼입 포함시켜 배합되어 제조되었다. 염소이온의 측정은 7일간 양생 후 수분 추출 방법을 이용하여 측정하였다. 실험을 통해 염소이온 고정화 능력이 결합재 종류 및 치환률에 의존하고 있음을 확인하였고, 총 염소이온량의 증가는 염소이온 고정화능력을 제한하여 결론적으로 염소이온 고정화를 감소시키고 있음을 보였다. 본 연구에서 최대 30%의 치환율을 가진 PFA와 60%의 치환률을 가진 GGBFS의 경우는 OPC보다 염소이온고정화 능력이 작았으며, SF의 치환률의 증가는 고정화를 감소시키고 있음을 확인하였으며, 이는 포졸란계 재료의 잠재 수화반응 혹은 공극수의 pH 저하등의 이유로 판단된다. 재령 7일에서의 염소이온의 고정화능력은 염해부식에 대한 저항성으로 나타내어지며, 염분을 혼입한 경우의 고정화능력의 순서는 30%PFA > 10%SF > 60%GGBFS > OPC로 나타났다. 더욱이 염소이온의 고정화 거동은 Langmuir isotherm 및 Freundlich isotherm으로 잘 표현될 수 있음을 보였다.