기존의 전자 기판에서 땜납으로 사용되고 있는 Sn-Pb계 합금을 대체하기 위한 새로운 합금을 개발하기 위하여 열역학을 이용한 상평형계산을 통해 얻은 다원계 상태도를 바탕으로 적정한 녹는점과 용융구간을 가지는 Sn-Bi-In-Zn계 솔더합금을 설계하였다. 설계된 합금을 제작하여 XRD, DSC및 EDX로 분석하여 상의 확인,조성분석 및 고상점과 액상점 등의 녹음 거동을 확인하였다. 또한 열처리에 따른 미세구조의 변화를 관찰하였고, 이러한 조직변화가 기계적 성질에 미치는 영향을 경도실험과 인장실험을 통해 연구하였다.

In relation to the preparation of Langmuir-Blodgett thin film, four kinds of N-alkylpyridiniurn bromide were synthesized. The values of surface tensions of these materials, measured with a Traube stalagmometer, gave the relationship between the critical micells hydrophobic radical and between CMC and temperature. Values of thermodynamic properties(δH0m, δS0m, δG0m,) for the formatoin of micelle were also obtained. Experiments gave the following results; at the temperature range between 40 and 60℃, CMC of Hexadecyl-, Octadecyl-, Eicosyl-, and Docosyl-Pyridinium Bromide were 7.64×10-4~9.13×10-4, 3.85×10-4~4.60×10-4, 2.00×10-4~2.39×10-4, and 1.07×10-4~1.28×10-4 mol/l, respectively. Surface tension, γCMC, of those were 33.49~36.00, 34.78~37.61, 35.49~37.61 and 38.76~55.80 dyne/cm, respectively, The relationship between CMC and the mumber of carbon atoms in the hydrophobic radical, N was expressed as follows : Log(CMC)=A-BN where A and B are constants. At the temperature range between 40 and 60℃, the change of Gibbs evergy (δGm) for one methylene group (-CH2-) were -0.65RT, respectively, The minus values of enthalpy change (δHm) suggest that the formation of micelle is exothermic. Additionally, the overall increase in the entropy change (δSm) with respect to the temperature increase suggests that the formation of micelle is attained by a exothermic enthalpy directed process.

장어통발의 P.P깔때기 살과 대나무 깔때기 살의 탄성을 측정하고 측면 구멍을 막은 통발과 원형의 유수저항, 침강시간 및 미끼의 냄새확산 등을 관찰한 다음 해상어획 시험을 행한 결과는 다음과 같다. 1. P.P 깔때기 살의 탄성은 대나무 살보다 훨씬 작고, 하중이 증가할수록 탄성회복도는 감소하였다. 2. 플라스틱 장어통발의 유수저항 R(kg)는 유속 V(m/sec)에 따라 다음 관계식으로 나타낼 수 있다. R=0.36V 상(2.01) 3. 장어통발의 침강시간은 측면 구멍을 막은 경우 수면상에서의 완전 침수까지 1~2초 정도 원형보다 지연되나 그 후의 침강속도는 거의 차이가 없었다. 4. 통발 내의 미끼 수용액은 측면 구멍을 많이 막을수록 원형보다 입구쪽으로 집중되어 확산되었다. 5. 측면 구멍을 일부 막은 통발과 원형을 가지고 어획시험을 한 결과 통발당 평균 어획미수나 평균어획량의 어획성능에 있어서 뻘로 된 어장에서는 차이가 없는 것 같다.

목적: 본 연구는 아동의 운동발달 수준에 따른 손가락의 최대근력과 신경역학적 특성을 규명하기 위한 예비연구 이다. 방법: 아동의 운동발달 수준을 평가하기 위하여 경기도 S시 지역아동발달센터에서 모집한 초등학교 2-4학 년생 31명을 대상으로 Movement Assessment Battery for Children-2(MABC-2)를 실시하였다. 이 중 보호자와 아 동이 본 실험에 참여하는 것을 동의한 일반아동 8명과 운동발달 지연이 의심되는 아동 6명을 대상으로 힘 센서를 사용하여 각각 왼손, 오른손, 양손의 손가락 최대근력을 측정하였다. 측정된 최대근력을 통해 각 조건의 손가락 최대근력과 신경역학적 특성을 의미하는 수지독립성을 산출하였으며, 집단의 차이를 규명하기 위해 독립 t-검정 및 맨-휘트니 U 검정을 실시하였다. 결과: 운동발달에 지연이 의심되는 아동은 일반아동과 동일한 수준의 손가락 근력을 지녔다. 그러나 양손 간 수지독립성의 경우 운동발달 지연이 의심되는 아동의 비우세 손이 더 독립적으로 움직이는 특성을 보였다. 결론: 운동발달 지연이 의심되는 아동이 일반아동에 비해 소근운동기술이 부족 한 원인은 손가락 근력의 문제라기보다 손가락 힘을 발생시킬 때 나타나는 신경역학적 특성인 수지독립성의 차이에 따른 것으로 생각된다. 이러한 연구결과는 운동협응 능력이 부족한 아동들의 손가락 제어 기전을 이해하기 위 한 기초자료로 활용될 수 있을 것이다.

화강암 석산에서 1번 면, 2번 면 및 3번 면으로 알려진 세 직교하는 분할면의 강도 특성을 검토하였다. R, G 및 H 공시체는 거창 및 합천 지역에서 분포하는 쥬라기 화강암류의 블럭 샘플로부터 획득하였다. 이들 세 공시체의 장축의 방향은 세 면 각각에 수직이다. 세 면에 대한 판별에 유용한 주요 사항은 다음 과 같다. 첫째, R, G 및 H 공시체의 일축압축강도와 관련된 세 그래프의 스케일링 특성을 보여 주는 도면을 작성하였다. 강도의 증가에 따라 세 공시체의 그래프는 H < G < R의 순으로 배열한다. 공시체 내부의 조직 균일도를 지시하는 세 공시체에 대한 그래프의 경사각을 비교하였다. H 공시체(θH, 24.0°~37.3°)에 대한 상기 한 각이 세 공시체 중에서 가장 낮다. 둘째, 두 공시체의 평균압축강도의 조합을 나타내는 RG, GH 및 RH 공시체의 세 그래프와 관련된 스케일링 특성을 도출하였다. 다양한 형태를 취하는 이들 세 그래프는 GH < RH < RG의 순으로 배열한다. 섯째, 강도차(Δσt)와 경사각(θ) 사이의 상관도를 작성하였다. 위의 두 파라미터 는 -0.003의 지수(λ)를 갖는 지수함수의 상관성을 보여 준다. 두 화강암에서, RH-그래프의 경사각(θRH)이 가장 낮다. 넷째, 세 공시체에 대한 세 종류의 압축강도 그리고 각 공시체에 가해진 압축하중에 평행 배열하는 두 조의 미세균열에 대한 다섯 파라미터 사이의 상관관계를 보여 주는 여섯 유형의 도면을 작성하였다. 거창 및 합천화강암에 대한 이들 도면으로부터, 빈도수(N, 0.872) 및 밀도(ρ, 0.874)와 함께 총 길이(Lt)에 대한 상관계수(R2)의 평균값(0.877)이 가장 높다. 또한, 세 공시체의 최소(0.768) 및 최대(0.804)의 압축강도에 비하여 평균압축강도와 관련된 상관계수의 값(0.829)이 보다 높다. 다섯째, 거창화강암의 세 공시체에서 발달된 상기의 두 조의 미세균열과 평행한 방향으로 측정한 압열인장강도의 분포 특성을 도출하였다. 관련 도면으로부터, R, G 및 H 공시체에 해당하는 이들 인장강도에 대한 세 그래프는 H(R1+G1) < G(R2+H1) < R(R1+G1) 의 순을 보여 준다. 인장강도에 대한 세 그래프의 배열순과 압축강도에 대한 세 그래프의 배열순과 상호 부합한다. 따라서, 세 공시체의 압축강도는 상기한 세 유형의 인장강도와 상호 비례한다. 여섯째, 상기한 세 그래프에서 도출한 각 누적수(N=1~10)에 해당하는 세 인장강도 그리고 각 그래프에 해당하는 다섯 파라미터의 값 사이의 상관 계수를 도출하였다. 10개의 상관도에서 도출한 각 파라미터에 대한 상관 계수의 평균값은 밀도(0.763) < 총 길이(0.817) < 빈도수(0.839) < 평균 길이(Lm, 0.901)  중앙 길이(Lmed, 0.903)의 순으로 증가한다. 일곱째, 세 공시체에 대한 일축압축강도 그리고 압열인장강도 사이의 상관도를 작성하였다. 상기한 상관도는 세 종류의 압축강도 그리고 다섯 그룹(A~E)의 인장강도를 근거로 아홉 유형으로 분류하였다. 관련 도면으로부터, 최소압축강도를 제외한 평균 및 최대압축강도와 함께 인장강도가 증가할수록, 상관계수의 값은 급격하게 증가한다.

탄소섬유는 경량이면서 높은 기계적 특성 때문에 우주항공, 선박, 자동차, 토목 및 건축과 같은 산업분야에서 그 어느 때 보다 더 광범위하게 적용되고 있다. 본 연구는 섬유혼입률 및 섬유길이 변화에 따른 탄소섬유 보강시멘트 복합재료( CFRC)의 역학적 특성과 휨 거동을 분석하였으며, 또한 자연 낙하시험에 의한 모르타르 시편에 대한 내충격성을 비교, 검토하였다. 더불어, 탄소섬유(CF)의 혼입률은 0.5%, 1.0%, 2.0% 및 3.0%로 변화를 주었으며, 각각의 섬유길이는 6 mm와 12 mm를 사용 하였다. 실험결과, 플로우 값은 탄소섬유의 뭉침현상으로 인해 유동성 측면에서 매우 불리하였으며, 단위용적질량은 다소 감소하였다. 특히, 압축강도는 탄소섬유 혼입량이 증가함에 따라 감소하는 것으로 나타내었다. 반면 휨 강도는 섬유 길이가 12 mm이고 2% 혼입한 것이 가장 높은 휨 강도를 보였다. 내충격성 시험결과, 보통 모르타르 시편은 완전파괴까지의 낙하횟수가 2∼3회 정도 걸리지만 반면 CFRC 시편은 섬유혼입량이 증가함에 따라 다소 차이가 있지만, 섬유길이가 12 mm이고 섬유혼입량 2% 인 경우 충격에 대한 저항성이 가장 높았다.

Mechanical properties of concrete such as compressive strength and elastic modulus are affected by the moisture inside the concrete members. Concrete specimens with various diffusion conditions are tested and the relations between the pore relative humidity and mechanical properties are suggested based on the experimental results. Suggested models are applied to the experimental results in the previous researches and the comparison results show that the models are reasonable.

This paper describes the mechanical properties of high strength concrete with 1,600 MPa strength steel fiber. The fiber aspect ratio and fiber volume fraction used in this study is 80 and 0.75%. The Cylindrical specimens with ∅150×300 mm and the prisms with 150×150×550 mm were mad and tested in accordance with KS F2403 and ASTM C1609. As the result, specimens with high strength fiber has superior performance then that with normal strength fiber.

The purpose of this study is to investigate the mechanical properties of cold-mixed recycled asphalt (CMRA) using Nano-TiO2 carrier. As a result, mechanical properties of CMRA using Nano-TiO2 carrier was confirmed to be superior than CMRA using commercial TiO2. Also, it was confirmed to be performance of equal or higher than of existing technology.

In this study, as series of studies to provide how to apply coal gasification slag(CGS) as one of byproducts for high strength concrete, from a newly introduced power generation method in Korea, the possibility of using a mixed aggregate with 25 percent of CGS as a concrete residual were investigated. The results indicated that the compressive strength of concrete using CGS at early age was lower than that using CS, but compressive strength at 28 days showed similar levels of strength enhancement.

최근 남해안과 제주도 연안에는 5,000톤 이상의 괭생이 모자반이 유입되어 양식장과 조업에 큰 피해를 주고 있으며, 환경훼손 등 사회적 문제로 부각되고 있다. 괭생이 모자반에 존재하는 알긴산은 주로 의약품, 식품 등으로 활용되는 천연 고분자 물질이다. 하지만, 대량으로 활용할 수 있는 수요처가 확보되지 않아 본 연구에서는 괭생이 모자반을 활용한 바이오 폴리머를 구조물 보수용 폴리머 모르타르에 활용하기 위한 연구를 수행하였다. 응결특성 평가 시험에서는 바이오 폴리머가 12% 혼입된 L0BP12 배합은 합성폴리머만 혼입된 L12BP0 배합보다 종결시간이 최대 20%증가하는 것을 확인하였다. 흡수율 시험에서는 LOBP12 배합이 초속경 시멘트 배합인 Plain-URHC보다 0.36% 감소하는 것으로 나타나 바이오 폴리머 혼입으로 모르타르의 수밀성이 증가하는 것을 확인하였다. 압축 및 휨강도 시험에서는 바이오 폴리머의 혼입이 증가할수록 강도가 감소하는 경향을 나타내었고, KS F 4042 기준을 만족하는 최대 바이오 폴리머의 혼입률은 12%로 결정되었다. 또한, 재령 4시간 기준 부착강도는 Plain-URHC시험체 보다 모두 향상되었으며, 1 MPa 이상을 확보하여 바이오 폴리머의 혼입이 모르타르의 부착강도를 향상 시킬 수 있는 것을 확인하였다.

In this study, the cement composites incorporating Carbon Nanotube(CNT), Carbon Black(CB), and Carbon Fiber(CF) of 0.5, 1.0, and 1.5% of binder weight were evaluated to provide conductivity. In order to achieve this, compressive strength and electrical resistance were measured. As a result, the conductivity of cement composites incorporating CNTs was more sensitive than that of cement composites containing CB and CF.

This study investigates the effects of compressive strengths on mechanical properties of concrete with compressive strengths of 40 and 80 MPa. In this study, The steel fiber an aspect ratio of 64 and a tensile strength of 1,600 MPa used. As the result, There are no significant effect of fiber tensile strength on mechanical properties of normal strength SFRC. For high strength SFRC, Specimen with high strength fiber have superior performance then that with normal strength fiber.

This paper describes the effect of steel fiber volume fraction and aspect ratio on mechanical properties of SFRC with compressive strength of 40 MPa. In this study, The fiber volume fractions consist of 0.25%, 0.50% and 0.75% and aspect ratios are 64 and 80 used. The prisms with 150×150×550 mm were made and tested in accordance with EN-14651. Test results show that the superior flexural performance was observed in SFRC with higher fiber volume fraction and aspect ratio.

In this study, the rate of change of electrical resistance with respect to the strength and load of cement composites was investigated by incorporating Carbon Nanotube(CNT) at 0.25, 0.5, 0.75, 1.0% of the binder weight. Compressive strength test It was shown that the load of 30% was repeatedly applied to impart conductivity through the rate of change of electrical resistance. The incorporation rate of CNT greatly affected the compressive strength and the rate of change of electrical resistance.

The purpose of this study was to evaluate the mechanical properties and bond performance of epoxy paint containing graphene materials. Experiment result, it was confirmed that graphene materials are effective to improve the mechanical properties of the epoxy paint, but it is not effective to improve the bond performance.

순환유동층 보일러애시(CFBC ash)는 매년 발생량이 증가하고 있으며, 대부분 활용성이 제한되어 매립, 폐기되고 있는 실정이다. 순환유동층 보일러애시의 화학조성 주성분은 SiO2, CaO, CaSO4로써, 물과 반응하여 시멘트와 유사한 자기수경성을 가지고 있다. 본 연구에서 는 순환유동층 보일러애시의 자기수경성을 활용하여, 폴리머 혼입 보수 모르타르를 개발하기 위한 최적배합을 도출하고자 하였다. 폴리머 혼입 보수 보르타르 개발을 위해 순차적으로 3 Case의 배합을 설정하고 기초 물성을 확인하였다. 그 결과, 순환유동층 보일러애시에 실리카흄 10% 혼입과 폴리머 1.0% 혼입, 팽창재 3.5% 혼입에서 최적의 결과를 얻을 수 있었다.