The objective of this paper is to provide the feasibility of premixed type ternary blended aggregates using raw fly ash(Ra), crushed sand(CS) and sea sand(SS) by studying fresh properties of the concrete. Ra is varied from 2.5% to 10% with interval of 2.5% by weight of mixed aggregates. Test results indicates that the replacement of Ra by mixed aggregates with low quality crushed sand and sea sand resulted in decrease of slump and air contents due to increased viscosity.

The purpose of this study was to evaluate flowability of engineered cemetitious composite(ECC) Using blast furnace slag and fly ash as a binder in mixture. From the test result, flowability value of all ECC mixtures show good flowability and self compacting performance.

In this study, it was developed geopolymer concrete of alkali-activated using the mixed fly ash and blast furnace slag. and it was developed the interlocking block using the developed geopolymer concrete. In addition, the bending strength and water absorption rate of the interlocking block was tested by KS standard. The test results were as follows. The water adsorption ratio of the BSF4 specimen was under 10%, and the flexural strength of that was over 5MPa

The purpose of this study was to evaluate flowability of engineered cemetitious composite(ECC) Using blast furnace slag and fly ash as a binder in mixture. From the test result, flowability value of all ECC mixtures show good flowability and self compacting performance.

In this study, it was developed geopolymer concrete of alkali-activated using the mixed fly ash and blast furnace slag. and it was developed the interlocking block using the developed geopolymer concrete. In addition, the bending strength and water absorption rate of the interlocking block was tested by KS standard. The test results were as follows. The water adsorption ratio of the BSF4 specimen was under 10%, and the flexural strength of that was over 5MPa.

플라이애시가 시멘트의 대체재로 사용되면서 플라이애시는 콘크리트의 특성변화에 중요한 역할을 하고 있다. 본 연구에서는 보통 콘크리트와 플라이애시를 혼입한 콘크리트의 철근부식에 대한 저항성을 평가하였다. 부식속도가 가장 빠른 간만대 환경을 모사한 최적 건습 반복시험방법을 찾고 해양환경폭로시험장의 간만대에 장기간 노출된 시편의 철근부식모니터링 시험결과와의 비교를 통해 FA 혼입에 따른 OPC 대비 부식 지연비를 도출하였다. 반전지전위법에 의한 부식 모니터링 결과 인공해수에 3일간 침지 후 4일간 건조의 반복 조건보다는 염수 를 시편 상부에 침지시켜 염수 및 산소의 공급이 계속되는 염수 ponding 시험법이 부식을 촉진시키는 것으로 나타났다. 모든 시험법에서 OPC 에 비해 FA의 철근 부식이 지연되었다. FA의 철근부식 지연비율은 재령이 증가할수록 증가하였으며 OPC 대비 최대 27%까지 철근부식이 지 연되었다. 그 결과 플라이애시 콘크리트는 재령이 증가할수록 철근부식 저항성능이 향상됨을 알 수 있었다.

Geopolymer has recently emerged as an environmentally sustainable material considered to be an alternative to conventional Portland cement. Current study exhibits and discusses the results of experiment on the alteration in mechanical strength of fly ash-based geopolymer mortar activated by alkaline solution with three different sodium hydroxide solution concentrations (etc 10M, 14M and 18M) after exposure to elevated temperatures ranging from 100oC to 1000oC. Thegeopolymermotarexhibitedits strength increase after exposure at 100oC or 200oC ,followed bythe considerable strength loss in strength between 300oC and 700oC. However, the mortar strength rose slightly after exposure to temperature range from 800oC to 1000oC due to the viscous sintering process.

이 논문은 표면 차수벽형 석괴댐(Concrete-Faced Rock-Filled Dam) 콘크리트의 내구성능 개선에 관한 것이다. 댐은 영구 구조물이 며 그 중요성을 감안할 때 충분한 내구성능이 확보되어야 한다. 이 논문에서는 플라이애시와 PVA 섬유를 혼입함으로써 차수벽 콘크리트의 내 구성능을 개선하고자 하였으며, 플라이애시와 PVA 섬유 혼입율에 따른 내구성능 향상 검증을 위하여 기본물성 (강도, 소성수축, 자기수축)을 포함한 내구성능 검증 실험(염소이온 침투, 마모 저항성, 동결융해 저항성)을 수행하였다. 실험 결과, 플라이애시 15%와 PVA 섬유 0.1%를 혼 입하였을 때 내구성능 개선 효과가 뛰어난 것으로 나타났다. 검증된 차수벽 콘크리트의 현장 적용을 통해 표면 차수벽형 석괴댐의 안전성 및 내 구성 개선에 기여할 수 있을 것으로 판단된다.

This study was evaluated the field applicability of high fluidity concrete for pc sleeper using high volume fly ash.

This paper investigated the thermal and mechanical properties of high-volume fly ash concrete for potential application in mass concrete.

본 연구는 폴리머 기반 보수모르타르에 미분쇄된 플라이애시 치환율의 영향을 평가하였다. 주요변수는 양생온도와 미분쇄된 플라이애시의 치환율이다. 양생온도는 40℃, 20℃ 및 5℃로, 미분쇄된 플라이애시 치환율은 결합재 대비 0~35%로 변화하였다. 굳지 않은 모르타르에서는 플로우를, 굳은 모르타르에서는 재령별 압축강도, 응력-변형률 관계 및 탄성계수, 파괴계수를 측정하고, 주사전자현미경 및 엑스선회절기 분석을 수행하였다. 실험결과 보수모르타르의 플로우, 탄성계수 및 파괴계수는 미분쇄된 플라이애시 치환율 20~30%에서 가장 높은 성능을 발휘하였다. 또한 재령별 압축강도는 미분쇄된 플라이애시 치환율과 양생온도에 현저한 영향을 받았는데, 미분쇄된 플라이애시 치환율 20%에서 초기강도 발현율이 가장 높았다. ACI 209에서 제시하고 있는 콘크리트 재령별 압축강도예측모델에서 초기 및 장기재령 강도발현 계수는 미분쇄된 플라이애시 치환율과 양생온도의 함수로 일반화할 수 있었다. 미분쇄된 플라이애시가 첨가된 페이스트는 수화생성물을 나타내는 피크(peak)의 수와 강도(intensity)가 증가되고 플라이애시 입자주변에 CSH 겔이 형성되었다.

The expansive behaviour of heat-cured mortars containing fly ash was investigated. The use of fly ash(replacement 20%) to the mortar reduced the long term expansion. But increase of SO3 in cement led to increase the long term expansion, and gave impetus to the formation of monosulphate for elevated temperature.

In this study, it was evaluated air content properties of concrete using air-entraining agents for modified flyash.

Concrete strength is not only an important factor in design and quality control, but it also represents the overall qualityof concrete. The use of admixture has been increasingly prevalent in the recent cases of concrete production as a meansto improve the functionality of concrete. Of particular note, fly ash is added in either the cement or the ready-mixedconcrete production stage with the general mixing ratio being about 15%; however, using fly ash slows down the initialhydration of the binding material, which can in turn cause a delay in acquisition of strength. In this study, calcium sulfoaluminate (C4A3S; CSA) was added to improve the initial strength of cement after the use of fly ash, and its effect instrength improvement was analyzed. The substitution ratios of fly ash were 0, 10, 20 and 30%, and the amount of CSAadded to improve the initial strength was 8% of the fly ash weight. The results of the experiment showed that adding CSA resulted in high calorific values at peaks 1 and 2 of hydration heat, and an X-ray diffraction analysis showed thatthe amount of unhydrated materials was higher with increasing substitution ratio of fly ash. An increase in CSA wasalso shown to lead to a higher amount of ettringite being generated in the early ages. In conclusion, addition of 30% flyash and 8% CSA led to an ettringite production that was 3 times higher than the mixing ratio of fly ash, which effectivelyimproved the initial strength. The same phenomenon was observed in the electron microscope analysis. Based on theseresults, it was determined that adding CSA in an amount that equaled to 8% of fly ash weight can promote the productionof ettringite, thereby improving the initial strength, which gets reduced by the use of fly ash.

하수슬러지 자원화 처리 방안 중 하나인 고화처리는 시멘트 및 생석회 등의 무기계 재료를 고화공정의 첨가제로 사용하여 하수슬러지를 고화시켜 인공토양을 제조하는 기술로, 다른 자원화 방법과 비교하여 에너지 사용량이 적은 공법으로 재자원화율이 가장 높은 육상처리 방법이라 말할 수 있다. 환경부 국가환경기술정보센터의 자료에 따르면 2012년 4월 현재 국내 운영 중인 총 89개의 하수슬러지 처리시설 중 고화처리 시설은 12개소이며, 처리 가능 시설 용량은 2,668톤/일으로 전체 시설의 약 30%를 차지하고 있다. 본 연구에서는 슬래그 활성화 메커니즘을 기반으로 하고 자극제로 고칼슘 플라이애시인 열병합발전소 소각재와 제지슬러지 소각재를 활용하여 제조한 하수슬러지 고화재 CMD-SOIL 1000 (형원길 외, 폐기물학회 2012)을 국내 4곳의 하수슬러지 자원화 시설에 적용하여 설비 운용성을 평가하고, 최종 배출 고화물을 매립지의 복토재로 재이용하기 위해 관련 규정에 의거한 적합성을 평가하였다. 평가 결과 자원화 시설에서 설비 가동성과 관련하여 요구하는 항목인 고화재 이송 여부, 시간당 혼합 배치 수 및 배출량 그리고 하수슬러지 중량에 대한 고화재 적정 혼합비율을 모두 만족시키는 것을 확인할 수 있었다. 또한 유기성 오니를 고화하여 생산한 고화처리물을 매립시설의 복토재로 재활용하기 위한 규정인 ‘폐기물관리법 시행규칙 별표 5의 2’ 에서 정한 수소이온농도 12.4 이하, 수분함량 50% 이하, 투수계수 1.0×10-7cm/sec 이상 1.0×10-3cm/sec 이하, 일축압축강도 0.10MPa 이상 그리고 유해물질 함량 기준인 ‘토양환경보전법 시행규칙 제1조 5’ 에 따른 토양오염우려기준 중 2지역 이내인 기준치를 모두 만족하여, CMD-SOIL 1000은 기존 국내 하수슬러지 자원화 설비에 적합한 하수슬러지 고화재인 것으로 판단되었다.

하수슬러지 자원화 처리 방안은 소각, 건조, 탄화, 용융, 고화, 연료화, 퇴비화 등이 제안되고 있다. 그 중 고화처리는 다른 공법에 비해 건설비 절감, 처리공정 단순, 환경영향이 적다는 특징을 가지고 있다.하수슬러지의 고화처리 시 고화재 투입으로 인한 건조 중량 증가가 단점으로 언급되고 있으나, 하수슬러지를 이용하여 제조한 인공토양은 흙을 대체할 건설재료로 활용이 가능하여 천연토사의 절감과 인공토양의 판매로 인한 경제적인 장점을 지니고 있다. 본 연구에서는 슬래그 활성화 메커니즘을 기반으로 하고 자극제로 고칼슘 플라이애시를 활용하여 제조한 하수슬러지 고화재 CMD-SOIL 1000(형원길 외, 폐기물학회 2012)을 국내 하수슬러지 자원화 설비에 적용하여 배출된 고화물의 유효 자원으로써의 재활용 가능성을 평가하고자 하였다. 상기 고화물의 매립시설 복토재로 품질 적합성(폐기물관리법 시행규칙)을 선행 연구결과 확인할 수 있었으며, 다짐시험을 실시한 결과 연약지반 판정기준의 사질지반 기준(도로설계 편람, 2000)을 상회하는 값인 최적 함수비 49.1%와 최대 건조밀도 1.06g/cm²를 나타내어 지반침하에 대한 안정성 확보가 가능한 것으로 판단되었다. 또한 고화물과 자연 상태의 토사를 일정한 비율로 혼합한 토양에 페레니얼 그라이스를 파종하여 생육 특성을 살핀 결과, 발아초기에는 자연 상태의 토사의 비율이 높을수록 개체수가 많고 성장속도의 차이가 있었으나 재령이 지날수록 육안으로 관찰되는 차이가 없었으며, 파종 56일 이후에는 자연 상태의 토사만을 활용한 경우와 동일한 생육 상황이 관찰되었다. 따라서 고칼슘 플라이애시를 적용한 하수슬러지 고화물은 매립지 복토재 외에도 토지개량제 및 기반 성토재 등의 용도로 활용이 가능한 것으로 판단되었다.

This study is regarding the property evaluation of mortar for ‘ONDOL’ floor (Korean floor heating system) finishing with reduced drying and shrinking properties to use it in the form of ready-mixed concrete mortar. The mortar utilized furnace slag based inorganic binding agent NSB, which has the characteristic of CaO included in HCFA generated from the fluidized-bed-firing power plant. Based on the test results, it is judged that mortar for ‘ONDOL’ floor finishing based on NSB including HCFA can be used in the form of ready-mixed concrete. According to site test construction, the flow property was relatively poor because fine gravel at ready-mixed concrete factory was used. However, since finishing property, crack resistance and water content are good, it is believed that it can be used at construction site in the form of ready-mixed concrete mortar. More study on adhesion property with floor plate would be required in the future.

In this study, it was evaluated the carbonation properties of concrete by replacement of the flyash after it was ground by vibration mill and was modified chemically. Also, it was compared to 1day, 3day, 7day, 28day and 56day-strength of the concrete, respectively.

The objective of this study is to investigated the compressive characteristics properties used cement paste containing 20% fly ash with curing days.

Recently, the amount of the mineral admixture including fly ash and ground granulated blast-furnace slag was increased for the purpose of CO2 gas emission reduction in the concrete industry. However, in the case of korea, estimation model of strength development in concrete structural design code was prescribed a constant value according to cement type and curing method about the portland cement. therefore, the properties of strength development according to time of concrete using fly ash and ground granulated blast-furnace slag does not reflected estimation model of strength development. Accordingly, this paper was evaluated strength according to time on the concrete strength range using fly ash and ground granulated blast-furnace Slag and the strength development constant Bsc of concrete according to the kind of the mineral admixture and mixing ratio was proposed