논문 상세보기
pp.294-300
This study was carried out to investigate the possibility whether Metal Injection Molding (MIM) process could be applied to 95wt.%W-3.5wt.%Ni-1.5wt.%Fe heavy alloy in order to obtain an intricate shape. Methylcellulose was used in the injection molding for binder. was added in solvent substituting Fe powder and was doped on W-Ni premixed powder. When was added in solvent, the binder separation occurred for injection molding so that the matrix content was changed. Such problem was solved when was doped. In this study. the debinding process did not affect residual carbon content. The sintered microsouctures as addition methods of Fe element and the sintering temperature from to , which are around the temperature of liquid phase formation, were observed.
