This manuscript reports on compared color evolution about phase transformation of α-FeOOH@SiO2 and β-FeOOH@SiO2 pigments. Prepared α-FeOOH and β-FeOOH were coated with silica for enhancing thermal properties and coloration of both samples. To study phase and color of α-FeOOH and β-FeOOH, we prepared nano sized iron oxide hydroxide pigments which were coated with SiO2 using tetraethylorthosilicate and cetyltrimethyl-ammonium bro- mide as a surface modifier. The silica-coated both samples were calcined at high temperatures (300, 700 and 1000°C) and characterized by scanning electron microscopy, CIE L*a*b* color parameter measurements, transmission electron microscopy and UV-vis spectroscopy. The yellow α-FeOOH and β-FeOOH was transformed to α-Fe2O3 with red, brown at 300, 700°C, respectively.