논문 상세보기
pp.113-119
PURPOSES : The objectives of this study are to develop the eco-friendly pavement material using polyurethane binder and evaluate mechanical properties of the developed binder and concrete. METHODS : The bending beam test was conducted to select the sample candidates of polyurethane binder based on the bending strength. The characteristics of viscosity, curing time, and temperature change of sample binder was examined on different temperature conditions. The mechanical properties of polyurethane binder was estimated using the dynamic modulus testing. The indirect tensile strength test was conducted on polyurethane binder concrete with different gradation and binder content for evaluating the mechanical properties of concretes. RESULTS : Based on the beading beam test, four different binder samples were prepared for estimate the mechanical properties. The viscosity of polyurethane binder tends to increase with increase of liquid temperature and the hardening phenomenon begins 10 to 15 minutes at room temperature after mixing the resin and hardener. It is observed that the dynamic modulus of binder increases as loading frequency increases and change of modulus is found to be the highest in the PU-2I binder type. The PU-2I binder concretes shows the largest value of indirect tensile strength and indirect tensile energy. CONCLUSIONS : The use of polyurethane binder as pavement materials is capable of increasing the pavement performance and reducing the detrimental environmental effect during the highway construction.