진공사출금형용 STS316L 금속 다공체 제조 및 기계적 특성 KCI 등재

Fabrication and Mechanical Properties of STS316L Porous Metal for Vacuum Injection Mold

  • 언어KOR
  • URLhttps://db.koreascholar.com/Article/Detail/302985
구독 기관 인증 시 무료 이용이 가능합니다. 4,000원
한국분말야금학회지 (Journal of Korean Powder Metallurgy Institute)
한국분말재료학회(구 한국분말야금학회) (Korean Powder Metallurgy Institute)
초록

In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr-13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under 45 μm and over 180 μm, and then they were compacted with various pressures and sintered at 1210oC for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to 79 l/min·cm2. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.

저자
  • 김세훈(자동차부품연구원 소재융합디자인연구센터) | Se Hoon Kim
  • 김상민(자동차부품연구원 융합소재공정연구센터) | Sang Min Kim
  • 노상호(자동차부품연구원 융합소재공정연구센터) | Sang Ho Noh Corresponding Author
  • 김진평(자동차부품연구원 소재융합디자인연구센터) | Jin Pyeong Kim
  • 신재혁(자동차부품연구원 소재융합디자인연구센터) | Jae Hyuck Shin
  • 성시영(자동차부품연구원 소재융합디자인연구센터) | Si-Young Sung
  • 진광진(㈜동원테크 기술연구소) | Jin Kwang Jin
  • 김태안(㈜동원테크 기술연구소) | Taean Kim