In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr-13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under 45 μm and over 180 μm, and then they were compacted with various pressures and sintered at 1210oC for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to 79 l/min·cm2. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.

The mechanical and thermal properties of high temperature aluminate cementitious thermal storage material were investigated in this paper. Alumina cement was used as basic binder and the effect of the replacement of fly ash, silica fume, calcium sulfo aluminate and graphite for alumina cement was investigated.

용융아연도금(galvanizing)은 콘크리트 구조물의 철근 부식 문제를 해결하기 위해 사용된다. 용융아연도금 철근 콘크리트 보의 부착강도 영향에 대한 자료는 거의 없는 실정이다. 따라서, 이 연구의 목적은 용융아연도금철근이 콘크리트 보의 부착강도에 미치는 영향을 파악하는 데 있다. 용융아연도금철근을 사용한 부재와 일반철근을 사용한 부재의 구조실험을 통하여 겹침이음 거동과 부착강도 특성을 비교하였다. 실험변수로써 철근의 용융아연코팅 유무, 철근 직경과 겹침이음 길이를 고려하였다. 용융아연도금 철근콘크리트 보의 균열 및 파괴 특성을 파악하였다. 용융아연도금철근 콘크리트 보의 겹침이음부 휨 거동특성은 일반철근 콘크리트 보의 겹침이음부 휨거동과 유사한 것으로 나타난다. 또한, 용융아연도금철근의 사용은 일반철근을 사용할 때에 비해 콘크리트 보의 부착강도에 불리한 영향을 미치지는 않는 것으로 나타났다.