Nickel powders were prepared under solvothermal condition by precipitation from metal nitrates with aqueous ammonium hydroxide. The powders were obtained at in a temperature range of 190-250 oC for 6h. The morphology and size of nickel powders were studied as a function of reaction temperature. The synthesis of nickel crystalline particles is possible under a solvothermal conditions in ethylene glycol solution. Characterization of the synthesized nickel powders were studied by XRD, SEM(FE-SEM) and TG/DSC. X-ray diffraction analysis of the synthesized powders indicated the formation of nickel structure after reaction. The average crystalline sizes of the synthesized nickel powders were in the range of 200-1000 nm; and the distribution of the powders was broad. The shape of the synthesized nickel particles was almost spherical. The morphology of synthesized nickel powders changed with reaction condition. It was possible to synthesize nickel powders directly in ethylene glycol without reducing agent.

1. 서 론
2. 실험 및 방법
3. 고 찰
4. 결 론
Acknowledgenemt
References

• 박찬(국립창원대학교 메카트로닉스대학 나노신소재공학부) | Chan Park
• 배동식(국립창원대학교 메카트로닉스대학 나노신소재공학부) | Dong-Sik Bae Corresponding author