In this study, the chemical resistance of cement composites with polyvinyl alcohol (PVA) admixture, which are developed to enhance the durability and low tensile strength of concrete, was evaluated. The PVA admixture rates for cement composites were set as 0%, 1.0%, and 1.2%. The compressive, tensile, and flexural strengths of the cement composites were measured for each admixture rate. Results showed that the compressive, tensile, and flexural strengths increased by 1.3, 5.6, and 17.9 times, respectively, at the 1.2% PVA admixture rate, compared with the baseline (0% PVA). The chemical resistance of the cement composites was evaluated by measuring the mass loss after immersion in CaCl2, Na2SO4, and H2SO4 for 30, 40, and 50 days. The chemical resistance experiments indicated that the PVA admixture enhanced the chemical resistance of the cement composites by impeding the penetration of chemicals, thereby reducing mass loss. Therefore, the inclusion of PVA can improve the chemical resistance of the cement composites, while providing excellent mechanical properties.
본 연구에서는 콘크리트의 내구성 및 낮은 인장강도를 향상시키기 위해 개발된 폴리비닐알콜(PVA) 혼입 시멘트 복합 체의 내약품성을 평가하였다. 시멘트 복합체에 대한 PVA 혼입률은 0%, 1.0%, 1.2%로 설계되었다. 각 혼입률에 따른 시멘트 복 합체의 압축강도, 인장강도, 휨강도를 측정하였다. 결과적으로 1.2% 혼입률에서 압축강도는 1.3배, 인장강도는 5.6배, 휨강도는 17.9배 증가하였다. 내약품성 실험을 위해 염화칼슘, 황산나트륨, 그리고 황산 용액에 시멘트 복합체를 침지시킨 후 30일, 40일, 50일 후 질량 소실률을 측정하여 내화학성을 평가하였다. 내화학성 실험 결과, PVA 혼입은 약품의 침투를 방지하여 시멘트 복 합체의 내화학성을 향상시키는 것으로 나타났다. 총체적으로, PVA 혼입은 시멘트 복합체의 내화학성을 향상시키는 동시에 강도 특성을 제공하는 것으로 확인되었다.
2. 실험 설계 및 사용 재료
2.1 실험 변수
2.2 사용 재료
2.3 실험체 제작
2.4 실험 방법
3. 실험 결과 및 분석
3.1 압축강도
3.2 인장강도
3.3 휨강도
3.4 섬유 혼입률에 따른 강도 변화 분석
3.5 내화학성 실험 결과
3.6 PVA 섬유 혼입률에 따른 내화학성 분석
3.7 약품 침지 기간에 따른 내화학성 분석
3.8 약품에 따른 내화학성 분석
4. 결 론
감사의 글