PURPOSES : This study was conducted to evaluate the physical properties of the RAP 50 asphalt mixture containing polymer modified rejuvenator and warm-mix additive to improve the recycling rate of RAP and reduce CO2 emission. METHODS : Mix design of Polymer Modified Warm-mix Asphalt Mixture(RAP 50), and Hot Mix Asphalt Mixture(RAP 30) were produced and the properties of asphalt mixture such as Marshall Stability, ITS, Deformation Strength, TSR, and Dynamic Stability were compared between the two asphalt mixtures. RESULTS : The RAP 50 asphalt mixture showed superior or similar performances compared to the RAP 30 asphalt mixture in all the tests conducted. The results of the Marshall stability and dynamic stability in particular were 13,045N and 3,826 pass/mm, which were 11.37% and 76.7% greater than the RAP 30 asphalt mixture, which indicated that high plastic deformation resistance may be expected. CONCLUSIONS : The results obtained from laboratory tests on the two types of mixtures indicated that the use of polymer modified rejuvenator and warm-mix additive not only allows to increase the proportion of RAP but also improves its properties under lower temperature condition than RAP 30 asphalt mixture. Additionally, it was confirmed that plastic deformation resistance was high and moisture resistance and crack resistance were improved for a RAP 50 asphalt mixture.

1. 서론
2. 실험개요
    2.1. 사용재료
    2.2. 배합설계
3. 아스팔트 혼합물 품질 평가
    3.1. 마샬안정도 시험
    3.2. 간접인장강도 시험
    3.3. 변형강도 시험
    3.4. 인장강도비 시험
    3.5. 휠트래킹 시험
4. 시험 결과 및 분석
    4.1. 마샬안정도 시험결과
    4.2. 간접인장강도 시험결과
    4.3. 변형강도 시험결과
    4.4. 인장강도비 시험결과
    4.5. 휠트래킹 시험결과
5. 결론
감사의 글

• 박수민(정회원 · 전북대학교 토목공학과 석사과정) | Park Sumin
• 임치수(정회원 · 전북대학교 토목공학과 박사) | Lim Chisu
• 장대성(정회원 · 전북대학교 토목공학과 박사) | Jang Daeseong
• 윤상혁(정회원 · (주)윤성산업개발 이사) | Youn Sanghyeok
• 이재준(정회원 · 전북대학교 토목공학과 교수) | Lee Jaejun (Professor(Ph.D.) Department of Civil Engineering, Jeonbuk National University, 567, Baekje-daero, Deokjin-gu, Jeonju-si, Jeollabuk-do 54896, Korea) 교신저자