Carbon molecular sieve (CMS) membrane surpasses the upper-bound trade-off and plasticization phenomenon of polymer membrane. Recently, supported CMS membranes have been investigated to provide both high performance and mechanical strength. Herein, we have investigated the supported CMS hollow fiber membranes on low-cost alumina hollow fiber. To prepare the thin and uniform layers, the dip-coating parameters for intermediate and polymeric layers were varied in terms of the withdrawal rate and solution viscosity, respectively. Then, in order to confirm its feasibility in real industry, mixture gas was permeated through prepared CMS membranes. Moreover, the property of long-term stability was characterized in harsh conditions and further modified.

To separate olefin from paraffin efficiently, highly selective and permeable carbon molecular sieve (CMS) membrane has been employed. Especially, supported CMS membrane could offer high permeance and mechanical strength. However, it has been limited to flat or tubular type membranes despite a lower packing density due to a difficult manufacturing process of hollow fiber membrane. Thus, we have optimized the process to prepare the CMS membrane on alumina hollow fiber. To coat a defect-free thin alumina intermediate layer, the withdrawal speed during dip-coating process was varied, and the viscosity of polymer solution was controlled to form uniform layer. Then, the pyrolyzed CMS membrane was tested in propylene/propane mixture gas system as well as single component. Moreover, a long-term performance was evaluated in harsh conditions.

본 연구에서는 sol-gel법을 이용하여 세라믹 중공사 지지체 표면에 합성된 sol을 dip coating하고 활성층을 형성시켜 한외여과막을 제조하였다. 코팅 횟수 및 코팅 용액의 조성에 따른 코팅층 변화를 확인하여, 결함을 최소화하고 균일하게 제조할 수 있는 조건을 확립하고, 소결 후 투과 특성 측정을 통해 소결 온도의 영향을 고찰하였다. 제조된 한외여과막은 분획분자량(Molecular Weight Cut-Off, MWCO)과 gas-liquid displacement porometer (GLDP), liquid-liquid displacement porometer (LLDP)를 이용하여 기공크기를 측정하고 분리막의 성능과 기공크기의 연관성을 연구하였다.