Carbon molecular sieve (CMS) membrane surpasses the upper-bound trade-off and plasticization phenomenon of polymer membrane. Recently, supported CMS membranes have been investigated to provide both high performance and mechanical strength. Herein, we have investigated the supported CMS hollow fiber membranes on low-cost alumina hollow fiber. To prepare the thin and uniform layers, the dip-coating parameters for intermediate and polymeric layers were varied in terms of the withdrawal rate and solution viscosity, respectively. Then, in order to confirm its feasibility in real industry, mixture gas was permeated through prepared CMS membranes. Moreover, the property of long-term stability was characterized in harsh conditions and further modified.

To separate olefin from paraffin efficiently, highly selective and permeable carbon molecular sieve (CMS) membrane has been employed. Especially, supported CMS membrane could offer high permeance and mechanical strength. However, it has been limited to flat or tubular type membranes despite a lower packing density due to a difficult manufacturing process of hollow fiber membrane. Thus, we have optimized the process to prepare the CMS membrane on alumina hollow fiber. To coat a defect-free thin alumina intermediate layer, the withdrawal speed during dip-coating process was varied, and the viscosity of polymer solution was controlled to form uniform layer. Then, the pyrolyzed CMS membrane was tested in propylene/propane mixture gas system as well as single component. Moreover, a long-term performance was evaluated in harsh conditions.

본 연구에서는 sol-gel법을 이용하여 세라믹 중공사 지지체 표면에 합성된 sol을 dip coating하고 활성층을 형성시켜 한외여과막을 제조하였다. 코팅 횟수 및 코팅 용액의 조성에 따른 코팅층 변화를 확인하여, 결함을 최소화하고 균일하게 제조할 수 있는 조건을 확립하고, 소결 후 투과 특성 측정을 통해 소결 온도의 영향을 고찰하였다. 제조된 한외여과막은 분획분자량(Molecular Weight Cut-Off, MWCO)과 gas-liquid displacement porometer (GLDP), liquid-liquid displacement porometer (LLDP)를 이용하여 기공크기를 측정하고 분리막의 성능과 기공크기의 연관성을 연구하였다.

Membrane separation processes have been widely used in water purification or gas separation applications because of their process simplicity, low cost operation and small footprint. Nowadays, applications of ceramic membranes with high thermal, chemical and mechanical resistance has rapidly grown in new separation applications where the polymeric membranes cannot be used (e.g., high temperature, strong acidic/basic or solvent-contained corrosive feed solution). In this study, robust ceramic hollow fiber membranes were prepared by extrusion-phase inversion followed by sintering. The effects of preparation conditions on membrane characteristics were studied to improve the separation performance of ceramic membranes. In addition, a variety of modification methods and applications based on ceramic hollow fiber membranes will be discussed.

본 연구에서는 sol-gel법을 이용하여 균일하고 결함을 최소화한 세라믹 한외여과막을 제조하였다. 알루미나 중공 사 정밀여과막 지지체의 기공 크기를 줄이기 위해, 합성된 boehmite sol과 sol-ethanol 혼합 용액을 사용하여 dip coating법으 로 지지체 표면 위에 γ-알루미나 활성층을 형성시켰다. pristine sol을 이용하여 4회 이상 코팅했을 경우 박막층의 두께가 상당히 증가하여 균열 및 박리현상을 야기시키고, 3회 코팅을 진행하였을 경우 표면 결함이 최소화된 최적의 시료를 얻을 수 있었다. 또한, 소결 온도가 γ-알루미나 활성층의 기공 크기에 미치는 영향을 분석하였다. 소결 온도가 1000°C일 때 가장 높 은 순수 투과도 값을 보였으며, 10 nm 크기의 dextran 분획분자량(molecular weight cut-off (MWCO) : 51 kDa)이 관찰되었다. 600, 800°C에서 소결한 막의 경우, 12 kDa MWCO (dextran 5 nm)를 갖는 것으로 확인되었다. 결과적으로, 코팅 용액의 조성은 박막층의 두께에 큰 영향을 주었고, 소결 온도에 따라 분획분자량이 크게 영향을 받는 것을 알 수 있었다.