The effect of the laser beam diameter on the microstructure and hardness of 17-4 PH stainless steel manufactured via the directed energy deposition process is investigated. The pore size and area fraction are much lower using a laser beam diameter of 1.0 mm compared with those observed using a laser beam diameter of 1.8 mm. Additionally, using a relatively larger beam diameter results in pores in the form of incomplete melting. Martensite and retained austenite are observed under both conditions. A smaller width of the weld track and overlapping area are observed in the sample fabricated with a 1.0 mm beam diameter. This difference appears to be mainly caused by the energy density based on the variation in the beam diameter. The sample prepared with a beam diameter of 1.0 mm had a higher hardness near the substrate than that prepared with a 1.8 mm beam diameter, which may be influenced by the degree of melt mixing between the 17-4 PH metal powder and carbon steel substrate.

본 연구에서는 표준화된 곰피추출물의 항산화 및 콜레 스테롤 개선에 대한 효능평가를 통해 건강기능식품 소재로서의 가치를 검토하기 위해 총 폴리페놀, 총 플라보노이드 및 dieckol 함량을 측정하였으며 DPPH, ABTS radical 소거능, reducing power 및 FRAP 활성을 통하여 곰피추 출물의 in vitro 항산화 활성을 조사하였고 표준화된 곰피 추출물의 HMG-CoA reductase 저해 활성 및 세포 내 콜레스테롤 생성 억제 효능을 평가하였다. 표준화된 곰피추출물의 총 폴리페놀, 총 플라보노이드 및 dieckol 함량은 각각 9.64±0.04 mg GAE/g, 2.72±0.08 mg RE/g, 27.42±0.66 mg/g 으로 나타났다. 표준화된 곰피추출물의 in vitro 항산화활 성, HMG-CoA reductase 저해활성 및 세포 내 콜레스테롤 생성 억제 효능은 농도의존적으로 증가하는 경향을 보였으며 이는 표준화된 곰피추출물에 함유되어 있는 페놀성 화합물에 기인된 효능으로 사료되며 항산화성분, 항산화 효과, 콜레스테를 개선 효능간의 상관관계가 있음을 확인 하였다. 향후, 표준화된 곰피추출물에 대한 in vivo 모델 에서의 전임상 연구 및 작용기전 입증되면 인체적용시험을 통해 이중기능성을 갖는 건강기능식품의 개발이 가능할 것으로 사료된다.