Pb-In솔더를 Si기판에 증착후 리플로시 가열 속도와 플럭스 사용에 따른 솔도볼 형성 거동, 증착 솔더이동, UBM(under Mump Metallurgy)의 Au층과 In간의 금속간 화합물 형성에 관하여 연구하였다. 가열 속도가 1˚C/min에서 10˚C/min, 20˚C/min로 증가하고, 플럭스를 적용한 경우 솔더볼은 용이하게 형성되었다. 특히 플럭스를 사용하여 형성시킨 솔더볼에서는 UBM Au층과 In간의 반응에 의하여 Auln 금속간 화합물이 형성되었다.

In this study, an attempt was made to fabricate TiAl as well as its in situ composite via combustion synthesis. The processing variable of the combustion synthesis which include aluminum content and the heating rate were found to affect the combustion temperature. The combustion temperature measured, however, was lower than the melting temperature of TiAl and the reaction product were found to include incomplet reaction products. Carbon was added in order to increase the combustion temperature as well as to form in situ reinforcements. The reaction products showed homogeneous microstructures with carbide phases formed within indicating that the addition of carbon increased the combustion temperature above the melting temperature of TiAl.

본 연구에서는 TiAl 금속간 화합물을 자전 고온 반응법을 이용하여 제조시 반응과정을 열시차 분석 방법으로 분석하였다. 합금 조성은 Ti-45at% Al, 53at%Al, 알루미늄 분말 크기, 승온 속도, 성형 밀도 등을 변화시켜 이들이 반응 과정에 미치는 영향을 관찰하였다. 분말이 미세할수록, 승온속도가 느릴수록, 성형 밀도가 낮을수록 반응 점화 온도 및 연소 온도가 감소하였으며, 고상 Ti와 고상 Al간의 반응정도가 증가하는 것이 관찰되었다. 고상 Ti와 고상 Al간의 반응에서 생성되는 것은 XRD 분석 결과 TiAl3상으로 확인되었다. 이에 비하여 반응 점화 온도가 알루미늄의 용융 온도보가 높을 경우에는 생성되는 상이 Ti3Al, TiAl상으로 확인되었다. 이러한 상의 생성 원인에 대하여 확산 계수 및 알루미늄의 용해도등의 요인으로 설명하였다.