For rear metallization with Al paste, Al back contacts require good passivation, high reflectance, and a processing temperature window compatible with the front metal. In this paper, the effect of the firing ambient during the metallization process on the formation of Al rear metal was investigated. We chose three different gases as ambient gases during the firing process. Using SEM, we observed the formation of a back surface field in N2, O2, and Air ambients. To determine the effect of the ambient on Voc, the suns-Voc tool was used. In this study, we described the mechanism of burn-out of organic materials in Al paste during the firing process. The oxygen ambient plays an important role in the burn-out process. We calculated the efficiency with obtained the back surface recombination velocities using PC1D simulation. It was found that the presence of oxygen during the firing process influenced the uniform back surface field because the organic materials in the Al paste were efficiently burned out during heating. The optimized temperature with oxygen flow shows an absolute efficiency of 19.1% at PC1D simulation.

Solar cells exhibit different power outputs in different climates. In this study, the temperature dependence of open-circuit voltage(V-oc), short-circuit current(I-sc), fill factor(FF) and the efficiency of screen-printed single-crystal silicon solar cells were studied. One group was fabricated with homogeneously-doped emitters and another group was fabricated with selectively-doped emitters. While varying the temperature (25, 40, 60 and 80˚C), the current-voltage characteristics of the cells were measured and the leakage currents extracted from the current-voltage curve. As the temperature increased, both the homogeneously-doped and selectively-doped emitters showed a slight increase in I-sc and a rapid degradation of V-oc. The FF and efficiency also decreased as temperature increased in both groups. The temperature coefficient for each factor was calculated. From the current-voltage curve, we found that the main cause of V-oc degradation was an increase in the intrinsic carrier concentration. The temperature coefficients of the two groups were compared, leading to the idea that structural effects could also affect the temperature dependence of current-voltage characteristics.

본 연구에서는 건강한 성인 여성을 대상으로 인삼 추출물을 함유한 스킨케어 제품의 시료 제시 방법과 여성들의 삶의 질 개선 효과 간의 상관 관계를 분석하였다. 삶의 질이란 질병이나 건강 상태가 일상생활에 미치 는 신체적, 정신적 그리고 사회적 영향에 대한 개인적인 반응을 나타내는 개념이다. 이에 저자들은 45명의 건강 한 성인 여성을 두 그룹으로 나누어 한 그룹(Group A)에는 브랜드 고유의 패키지를 유지한 인삼 크림 시료를 제공하였고, 다른 그룹(Group B)은 브랜드와 제품명을 알 수 없는 하얀색 통에 담은 동일한 시료를 제공하여 8주간 사용하게 하였다. 피부 관련 삶의 질 평가는 Skindex-16 설문지를 사용하여 시험 초기와 4주 후, 8주 후에 걸쳐 시행되었다. 시험 참여를 중지한 2명의 피험자를 제외한 43명의 Skindex-16 초기값의 평균은 22.70 ± 4.82점이었다. 8주 후, 그룹 A의 Skindex-16 지표는 초기값 23.30 ± 5.14에서 20.20 ± 4.83으 로, 그룹 B는 22.17 ± 4.58에서 20.52 ± 3.60로 통계적으로 유의한 정도로 개선되었다. 세부 항목에서는 그룹 A의 ‘증상’ 항목이 4주 후, ‘감정’ 항목이 8주 후에 통계적으로 유의하게 개선되었으며, ‘기능’ 항목은 어 느 그룹에서도 통계적으로 유의한 변화가 관찰되지 않았다. 또한, 총합과 세부 항목 모두 측정 시기 및 그룹에 따른 교호작용은 통계적으로 유의한 차이가 확인되지 않았다. 본 실험을 통해 인삼 크림이 포함된 스킨케어가 건강한 성인 여성의 삶의 질에 긍정적인 영향을 줄 수 있음을 확인하였으며, 스킨케어 행위 자체가 패키지에 대한 영향보다 삶의 질의 개선에 주는 영향이 큼을 추측할 수 있다. 장기적으로 ‘삶의 질’이란 기존의 피부과학 지표의 개선과 주관적 만족도의 개념을 넘어 신규한 화장품 효능 영역으로 추가적인 연구가 필요할 것으로 생 각된다.