        1.
        2004.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Nano sized FeAl intermetallic particles were successfully synthesized by plasma arc discharge pro-cess. The synthesized powders shouted core-shell structures with the particle size of 10-20 nm. The core was metallic FeAl and shell was composed of amorphous Because of the difference of Fe and Al vapor pressure during synthesis, the Al contents in the nanoparticles depended on the Al contents of master alloy.
        4,000원
        2.
        2004.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Iron-carbon nanocapsules were synthesized by plasma arc discharge (PAD) process under various atmosphere of methane, argon and hydrogen gas. Characterization and surface properties were investigated by means of HRTEM, XRD, XPS and Mossbauer spectroscopy. Fe nanocapsules synthesized were composed of three phases with core/shell structures. The surface of nanocapsules was covered by the shell of graphite phase in the thickness of nm.
        4,000원
        3.
        2004.08 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Fe nanopowders were successfully synthesized by plasma arc discharge (PAD) process using Fe rod. The influence of chamber pressure on the microstructure was investigated by means of X-ray Diffraction (XRD), Field Emission Scanning Electron Microscope (FE-SEM), Transmission Electron Microscopy (TEM) and X-ray Photoelectron Spectroscopy (XPS). The prepared particles had nearly spherical shapes and consisted of metallic cores (a-Fe) and oxide shells (FeO), The powder size increased with increasing chamber pressure due to the higher dissolution and ejection rate of H and gas density in the molten metal.
        4,000원