이 연구는 탄소섬유시트의 보강겹수와 보강위치에 따른 I형 PFRP 휨부재의 휨보강 효과에 대해 조사하였다. 또한, 탄소섬유시트로 보강한 PFRP 휨부재의 실험적, 이론적으로 확인하기 위해 유한요소해석을 실시하였으며, 휨실험 결과와 이론적 해석결과를 비교분석하였다. 휨실험 결과와 유한요소해석 결과는 이론적인 결과와 비교한 결과 일치하는 경향을 보였고, 휨보강 효과가 큰 탄소섬유시트 2겹을 보강한 시편에서 결과에서 오차가 가장 크게 발생하였다.

이 연구는 탄소섬유시트의 보강겹수에 따른 I형 PFRP 휨부재의 휨보강 효과를 조사하기 위해 길이 600mm의 PFRP 휨부재와 상하부 플랜지에 1mm 두께의 탄소섬유시트로 보강하여 휨실험을 수행하였다. 또한, 탄소섬유시트의 보강겹수와 보강 위치에 따른 I형 PFRP 휨부재의 휨보강 효과와 단면 감소량에 대해 조사하였다. 그 결과 2겹으로 보강하였을 때 휨강도와 휨강성이 증가함을 확인하였다.

In this paper, four point bending tests were carried out to analyse flexural strengthening effect by CFRP (Carbon Fiber Reinforced Polymer) layers for I shape PFRP (Pultruded Fiber Reinforced polymer) flexural member retrofitted with CFRP sheet. Comparing load-displacement relation and sectional stress distribution, the flexural strengthening effect by the number of CFRP layers was founded.

In recent years, fiber reinforced polymer plastic composites are readily available in the construction industry. Fiber reinforced polymer composite has many advantages such as high specific strength and high specific stiffness, high corrosion resistance, light-weight, magnetic transparency, etc. In this paper, we present the result of investigation pertaining to the flexural behavior of flange strengthened I-shape pultruded fiber reinforced polymer plastic (PFRP) member using carbon fiber sheet (CFRP sheet). Test variable is consisted of the number of layers of strengthening CFRP sheet from 0 to 3. From the experimental results, flexural strengthening effect of flange strengthened I-shape PFRP member using CFRP sheet is evaluated and it was found that 2 layers of strengthening CFRP sheet are appropriate considering efficiency and workability.

In recent years, fiber reinforced polymer plastic composites are readily available in the construction industry. Fiber reinforced polymer composite has many advantages such as high specific strength and stiffness, high corrosion resistance, light-weight, magnetic transparency, etc. In this paper, we present the result of investigation pertaining to the flexural behavior of flange strengthened I-shape pultruded fiber reinforced polymer plastic (PFRP) member using carbon fiber sheet (CFRP sheet). The number of layers of strengthening CFRP sheet, with a value of 0 to 3 was the test variables. From the experimental results, flextural strengthening effect of flange strengthened I-shape PFRP member using CFRP sheet is evaluated and it was found that 2 layers of strengthening CFRP sheet is appropriated considering efficiency and workability.

FRP products have been widely used in various fields of industry because of possessing high-strengths, corrosion resistance. Accordingly the waste FRP have also been increased and the effective recycling methods of waste FRP are needed. In this study, polymer mortar specimens were prepared with the various substitution amount of waste FRP powder. For finding the mechanical properties of polymer mortar added with waste FRP powder, compressive strength tests are conducted. From the test, we could find that compressive strength was increased with respect to the amount of waste FRP powder.

Recently, strengthening and repairing concrete structures are increasing due to the deterioration of concrete infrastructures. Carbon Fiber Reinforced Polymer Plastic (CFRP) system for strengthening concrete structures have emerged as an alternative to traditional strengthening techniques, such as steel plate bonding, section enlargement, and external post-tensioning. CFRP systems offer advantages over traditional strengthening techniques such as lightweight, noncorrosive, and relatively easy to install. In this paper, we present the structural design algorithm for the RC beams strengthened with CFRP sheet based on ACI 440. In addition, structural behavior of strengthened RC beams is investigated by varying the amount of CFRP sheets.

이 연구에서는 직교이방성 판의 좌굴 및 직교이방성 판요소로 구성된 구조용 압축재의 국부좌굴에 대한 해석적 연 구를 수행하였다. 섬유보강 폴리머 플라스틱 재료는 높은 비강도 및 비강성, 높은 부식저항성, 경량성 등 강재나 콘 크리트와 비교해서 많은 장점을 가지고 있다. 특히, 펄트루젼 생산 방식은 섬유보강 폴리머 플라스틱 재료의 여러 가지 생산방법 중 구조용 플라스틱 부재를 대량으로 생산하기에 가장 적합한 방법이다. 펄트루젼 생산방식은 부재 의 축을 따라 주요 보강섬유가 배치되기 때문에 이 재료는 직교이방성으로 간주된다. 그러나, 펄트루젼 섬유보강 플라스틱 부재는 낮은 탄성을 갖고 있고 얇은 판요소로 구성되어 있기 때문에 압축하중이 재하될 경우 좌굴이 발 생할 수 있다. 따라서, 이 부재를 설계하는데 안정성은 매우 중요한 문제가 된다. 이 연구에서는 기존의 연구를 따 라서 직교이방성 판 및 직교이방성 판요소로 구성된 압축재의 국부좌굴에 대하여 검토하였으며, 국내에서 생산된 직교이방성 판요소로 구성된 압축재의 국부좌굴강도를 계산하였다.

Oil in water (O/W)에멀젼에서 에멀젼 안정화제로 사용되는 고급알코올과 고급지방산이 O/W에멀젼의 유동특성에 미치는 영향을 점도와 rheograms으로 분석하였다. 고급알코올과 고급지방산의 탄소 체인 길이가 증가할수록 O/W 에멀젼의 점도가 상승하는 경향을 나타내었으며 고급알코올의 점도 상승 효과가 고급지방산보다 우수하였다. 또한 에멀젼 제조에 사용된 계면활성제의 친유부의 탄소 체인 길이에 유사한 스테아릴알코올과 세테아릴알코올의 점도 상승 효과가 가장 우수하였다. 고급알코올과 고급지방산이 첨가된 O/W에멀젼은 화장품 에멀젼이 보여주는 유동특성인 shear thinning을 나타내는 pseudo-plastic유체였다. 세틸알코올, 세테아릴알코올과 스테아릴알코올이 첨가된 O/W에멀젼은 thixotropy이었으며 농도가 증가할수록 thixotropic 현상이 증가하는 경향을 나타내었다. 또한 고급지방산보다는 고급알코올이 첨가된 O/W에멀젼이 더 thixotropic한 유동특성을 나타내었다. O/W에멀젼의 안정성과 관련된 점도상승과 사용감과 관련된 spreadability 향상을 위해 에멀젼 안정화제로 고급지방산보다는 고급알코올의 사용이 적합하리라 생각된다.

제타전위를 이용하여 이산화티탄의 분산 안정성을 평가하고 이를 통하여 분산안정도 향상에 응용하고자 하였다. 본 연구에서는 제타전위와 관련된 전기이중층, 전기영동, 등전점 및 전기 침투에 대하여 설명하였으며 측정이론을 기술하였다. H-S equation을 이용하여 수계에 분산된 미립자 이산화티탄의 pH변화에 따른 제타전위 변화를 측정하였으며 제타전위는 pH 3.0 ∼ 9.0에서 음의 값으로 측정되었다. 제타전위 값은 pH값 상승에 따라 절대값이 증가하였으며 분산액의 pH 8.0과 9.0에서는 지속적으로 분산이 유지되었다. 이를 통하여 제타전위가 이산화티탄의 분산에 영향을 미치며 제타전위의 절대값 크기가 수계에서 이산화티탄의 분산안정도에 중요한 역할을 하는 것으로 생각된다.