단순 침전법으로 제조한 CdZnS/ZnO 광촉매를 이용하여 가시광선하에서 메틸렌블루의 광분해 반응에 대한 연구를 수행하였다. X선 회절분석법과 UV-vis 확산반사 분광법 등을 이용하여 제조된 촉매들의 물리화학적 특성을 분석하였다. 그리고 CdZnS/ZnO 광촉매의 활성을 조사하고 CdS 및 TiO2와 비교 검토하였다. CdZnS/ZnO 광촉매는 자외선뿐만 아니라 400nm에서 600nm 범위의 가시광선 영역에 있어서도 우수한 광흡수 특성을 나타내었다. 가시광선하에서 메틸렌 블루의 광분해 반응에 대해서 CdZnS/ZnO 광촉매는 CdS 와 TiO2 보다 우수한 광촉매 활성을 나타내는 것을 알 수 있었다. 그리고 가시광선하에서의 메틸렌블루의 광분해 반응에는 광촉매 반응뿐만 아니라 감광반응도 관여하고 있음을 확인할 수 있었다.

We have studied the catalytic combustion of soot particulates over perovskite-type oxides prepared by malic acid method. The catalysts were modified to enhance the activity by substitution of metal into A or B site of perovskite oxide. In addition, the reaction conditions such as temperature and O2 concentration were investigated. The partial substitution of alkali metals into A site in the LaMnO3 catalyst, enhanced the catalytic activity in the combustion of carbon particulate and the activity was shown in the order: Cs＞K＞Na. For the La1-xCsxMnO3 catalysts, the catalytic activity showed the maximum value with x=0.3 but no more increase on the catalytic activity was shown with x＞0.3. For the La0.8Cs0.2MnO3 catalyst, the substitution of Fe or Ni increased the ignition temperature. The ignition temperature decreased with an increase of O2 concentration, however, no more increase in the catalytic activity was shown with O2 concentration＞0.2. The introduction of NO into reactants showed no effect on the catalytic activity.

Photocatalytic degradation of phenol was carried out with UV-illuminated TiO2- SiO2 in aqueous suspension. TiO2-SiO2 catalysts were prepared by sol-gel method from the titanium isopropoxide and tetraethylorthosilicate at different Ti/Si ratio and some commercial TiO2 catalysts were used as purchased. All catalysts were characterized by X-ray Diffraction(XRD) and BET surface area analyzer. The effect of reaction conditions, such as initial concentration of phenol, reaction temperature and catalyst weight on the photocatalytic activity was studied. In addition, TiO2-SiO2(49:1) prepared by sol-gel method showed higher activity than commercial TiO2 catalysts on the photocatalytic degradation of phenol. The addition of SiO2 into TiO2 hepled to increase the thermal stability of titania which suppressed the formation of anatase into rutile. The photocatalytic degradation of phenol showed pseudo-1st order reaction and the degradation rate increases with decreasing initial phenol concentration.