In the present work, water-based gold nanofluids were synthesized by the solution plasma processing (SPP). The size distribution and the shape of gold nanoparticles in the nanofluids were investigated using high resolution transmission electron microscopy (HR-TEM). The dispersion stability of gold nanofluids was characterized using zeta potential, as well. The thermal properties of gold nanofluids were measured by utilizing lambda measurement device. Nanofluids containing nanoparticles with in diameter were successfully synthesized. As diameter of nanoparticles decreased, dispersion stability of nanofluids increased and the enhanced ratio of thermal conductivity increased. The nanofluid with nanoparticles of in diameter showed approximately 3% improvement in thermal conductivity measurement and this could be due to the enhanced Brownian movement.

초강인 AISI 4340강을 850˚C에서 2시간 동안 오스테나이징 처리 후 수냉하고, 250, 400, 600˚C에서 각각 2시간 동안 템퍼링 처리를 하였다. AISI 4340강의 인장 특성은 상온에서 측정되었다. AISI 4340강 위에 니켈 전해도금된 것과 도금되지 않은 시편의 분극 특성이 3.5wt%NaCI 수용액과 인공해수에서 측정되었다. AISI 4340강위에 니켈 전해도금된 시편은 500mV(vs. Ag/AgCI)이하의 전위에서 부식 저항이 크게 향상되었다. 그러나 1A/cm2의 전류밀도에서 30분 이상 니켈 전해도금된 시편은 도금층에 불순물과 기공이 형성되었기 때문에 AISI 4340강의 부식 저항은 감소되었다. AISI 4340강의 수소취화형 응력부식균열을 여러 작용 응력과 음극인가전력에서 U-bend 시편을 이용하여 IN 3.5 wt% NaCI 수용액에서 조사되었고, 수소취화형 응력부식균열 거동은 주사전자현미경으로 조사되었다.