In this study, we optimized Pb-free Sn/Ni plating thickness and conditions were optimized to counteract the environmental regulations, such as RoHS and ELV(End-of Life Vehicles). The B10 life verification method was also suggested to have been successful when used with the accelerated life test(ALT) for assessing Pb-free solder joint life of piezoelectric (PZT) ceramic resonator. In order to evaluate the solder joint life, a modified Norris-Landzberg equation and a Coffin-Manson equation were utilized. Test vehicles that were composed of 2520 PZT ceramic resonator on FR-4 PCB with Sn-3.0Ag-0.5Cu for ALT were manufactured as well. Thermal shock test was conducted with 1,500 cycles from (-40±2)˚C to (120±2)˚C, and 30 minutes dwell time at each temperature, respectively. It was discovered that the thermal shock test is a very useful method in introducing the CTE mismatch caused by thermo-mechanical stress at the solder joints. The resonance frequency of test components was measured and observed the microsection views were also observed to confirm the crack generation of the solder joints.

초강인 AISI 4340강을 850˚C에서 2시간 동안 오스테나이징 처리 후 수냉하고, 250, 400, 600˚C에서 각각 2시간 동안 템퍼링 처리를 하였다. AISI 4340강의 인장 특성은 상온에서 측정되었다. AISI 4340강 위에 니켈 전해도금된 것과 도금되지 않은 시편의 분극 특성이 3.5wt%NaCI 수용액과 인공해수에서 측정되었다. AISI 4340강위에 니켈 전해도금된 시편은 500mV(vs. Ag/AgCI)이하의 전위에서 부식 저항이 크게 향상되었다. 그러나 1A/cm2의 전류밀도에서 30분 이상 니켈 전해도금된 시편은 도금층에 불순물과 기공이 형성되었기 때문에 AISI 4340강의 부식 저항은 감소되었다. AISI 4340강의 수소취화형 응력부식균열을 여러 작용 응력과 음극인가전력에서 U-bend 시편을 이용하여 IN 3.5 wt% NaCI 수용액에서 조사되었고, 수소취화형 응력부식균열 거동은 주사전자현미경으로 조사되었다.

면우 곽종석은 한주 이진상의 학설을 이어 받아 조선 말 최대의 학파라고 일 컬을 수 있는 한주학파를 선두에 서서 이끌면서 ‘개명한 도학자’로서 일생을 살 았다. 곧 그는 이진상의 竪看·橫看·到看의 三看法과 理發一途說, 心卽理說을 계 승하여 옹호하고, 이진상이야말로 공자와 맹자, 주자, 이황을 정통으로 계승하 였다고 주장하였다. 한주학파의 리발일도설과 심즉리설의 핵심은 심과 그 속에 있는 리의 주재성을 확보하여 주체에 철학적 무게를 실어주는 것이다. 이러한 철학적 작업은 단순히 이론적 영역에서만 머물지 않고, 가까이로는 어려운 시 기 도학자로서 삶을 살아가는 데 긴요한 것이었으며, 나아가서는 눈앞의 현실 을 인식하고 참여하는 데에도 그대로 영향을 미쳤다.