Back muscles play an important role in protecting the spine. Epidemiological studies have shown that loads imposed on the human spine during daily living play a significant role in the onset of low back pain. No previous study has attempted to correlate the response of the trunk musculature with the type of external load. The purpose of this study was to use surface electromyography (EMG) to quantify the relative demands placed on the back muscles while lifting loads in one hand. Forty asymptomatic, twenty year-old subjects stood while lifting loads of 10% of body weight(BW) unilaterally. All EMG data were normalized to a percentage of the EMG voltage produced during no-load standing(%EMG). Our major analysis involved a paired t-test for repeated measures. Of particular note was the fact that the ipsilateral 10% of BW condition produced statistically less % EMG change than did the contralateral 10% of the condition.

공진 주파수 온도 계수(τf)가 큰 음의 값을 가지는 (Li12Nd12)TiO3(LNT) 고주파 유전체를 1250˚C에서 1400˚C까지의 온도에서 2시간동안 소결을 하였고 소결후에는 소결온도보다 약간 낮은 1200˚C에서 5시간 동안 annealing을 실시를 하였다. 그리고 열처리에 의한 상, 미세구조의 변화를 X-ray, SEM을 통해서 분석하였으며, 열처리가 고주파 유전물성에 대해 미치는 영향에 대해서도 고찰하였다. 1300˚C에서 1350˚C 근방에서 소결시킨 재료는 Annealing효과에 의해 소결체에 균일한 입도 분포가 증진되었고 체적 밀도가 향상되었으며, 열처리 효과에 의해 품질계수(Q)값이 향상되었고 유전상수(εr)는 약간 감소하였으며 공진주파수 온도계수(τf)는 더 큰 음의 값을 가지게 되었다. 그러나 1350˚C이상에서 소결한 경우에는 비정상적인 입자 성장에 의해 밀도가 감소되며, 이에 따라 고주파 유전특성이 전반적으로 저하되었다.었다.