Hydrophobic nanodiamond (ND) were dispersed in engine oil (Helix Oil, Shell co.) as an additives to improve tribology properties. In this study, nanodiamond prepared by an explosive method was used. Tribology properties of both pure Helix oil and engine oil containing ND additive were evaluated. The rotating disks were made of Gray Cast Iron (240 Hv) and SKD11 (710 Hv). Surface topographies of the disks' wear tracks and friction coefficient were compared. The results show that nanodiamond-dispersed lubricants are capable of reducing these metals' wear loss. The friction coefficient is strongly affected to the hardness of wear track.

Multi shell graphite coated Ag nano particles with core/shell structure were successfully synthesized by pulsed wire evaporation (PWE) method. Ar and (10 vol.%) gases were mixed in chamber, which played a role of carrier gas and reaction gas, respectively. Graphite layers on the surface of silver nano particles were coated indiscretely. However, the graphite layers are detached, when the particles are heated up to in the air atmosphere. In contrast, the graphite coated layer was stable under Ar and atmosphere, though the core/shell structured particles were heated up to . The presence of graphite coated layer prevent agglomeration of nanoparticles during heat treatment. The dispersion stability of the carbon coated Ag nanoparticles was higher than those of pure Ag nanoparticles.