The optimum polymer gel electrolyte composition ratio was 23 : 66 : 11 wt% of P(VdF-co-HFP) : PVP =20 : 3), (PC: EC =44 : 22) and TEABF4. And the optimal thickness of polymer gel electrolyte was 50um . The electrochemical characteristics result of unit cell were 31.41 Fig of specific capacitance, and 3.21x10-3 S/cm of ion conductivity. Ion conductivity of polymer gel electrolytes decreased according to added PVP through impedance analysis, and it was higher in 7 wt%, but electrochemical characteristics of unit cell were better in 3 wt% PVP. And for excellent ion conductivity of polymer gel electrolytes, the use of a thin layer electrolyte(20um) was an effective method, but with unit cell application, the best thickness was 50um . Unit cell showed higher capacitance and more stable electrochemical performance when hot pressed between polymer gel electrolyte and electrode. This results from enhancement of the physical contact between the electrode and the polymer gel electrolyte and good accessibility of the liquid electrolyte to the electrode surface.

The electrodes were fabricated by compounding the commercial activated carbons and additives of conducting polymer with PVdF mono binder and PVdF-PVP mixed binders. The best performance of the electrodes fabricated with activated carbon(BP-20) and PVdF-PVP mixed binders showed in 88wt. ％ BP-20. 7wt. ％ conducting polymer and 5wt.％ PVdF-PVP mixed binder. The electrode exhibited excellent electrochemical characteristics having 8.16 W.h/kg of energy density, 34.77 F/g of specific capacitance, 0.67Ω of ESR.

High surface area and high pore volume activated carbon was prepared by KOH activation of rice hull. The electrodes were fabricated by compounding the commercial and rice hull activated carbons with PVdF and PVdF-PVP mixed binders without addition of conductivity improver. The electrodes fabricated with rice hull activated carbon and PVdF-PVP mixed binders showed the best performance because the PVP played as a pore-forming agent. The electrode exhibited excellent electrochemical characteristics having 7.9 W.h/kg of energy density, 33.5 F/g of speific capacitance, 0.7 Ω of ESR and good efficiency of self-discharge compared with that fabricated with commercial activated carbons.