        Ceramic welding backing material is a mullite-cordierite composite that is currently being used for welding processes in plant and shipbuilding. It is the optimal material for welding processes thanks to its extremely low thermal expansion coefficient and strong resilience against high temperature. However, due to the pollutants from welding such as iron and carbon, the entire amount of ceramic welding backing material is being land-filled after a single-time use. In this study, ceramic welding backing material was mixed with clay and kaolin to be used as a new ceramic body. A composition with 20 ~ 50% of ceramic welding backing material showed sufficient plasticity, and when fired at 1,250oC, it was deemed available for ceramic block and others with the porosity of 2.27 ~ 5.94%, water absorption ratio of 0.99 ~ 3.96% and bending strength of 720 ~ 810 kgf/cm2. In addition, color ceramic body, which was made from a waste welding backing material, of which iron was partially removed, added with 3wt% of high temperature pigment and fired at 1,250oC, displayed the unique color of the pigment, meaning that waste welding backing material could be used for ceramic bodies of a variety of colors.