In Article 10 of our Constitutional Law in our country prescribed that “All of our people have a dignity as a humanbeing and value also have a right to puruse happiness” It has clearly defined that the human dignity is the highest value of the rule. The term “human rights” means any of human dignity, worth, liberties and rights which are guaranteed by the Constitution and Acts of the Republic of Korea or recognized by international human rights treaties entered into and ratified by the Republic of Korea and international customary law. The main objectives of the human rights are to realize the dignity and worth of the human person in order to contribute to the safeguard of the basic order of democracy. It is very important to protect and promote the inalienable and fundamental human rights of all individuals. This paper is a study on guaranteeing the Human Rights of convicted prisoners. In this thesis, aimed at groping improvement device of the convict system to establish the human rights. It is impossible only effort of The prison officer for the national human rights safeguard and improvement of the basic human, a continuous interest should be required as well as a new posture of the national consciousness for the human rights.

급냉응고법을 이용하여 고용한도 이상으로 Mn량을 첨가할 때 Mn량에 따른 인장특성의 변화와 시효특성을 조사하였다. 원심분무법으로 AI-4.7%Zn-2.5%Mg-0.2%Zr합금에 Mn량을 각기 달리 첨가한 급냉응고 분말을 제조 하였다. 이 분말을 냉간압축, 진공 탈가스처리를 한 후 15:1로 압출하여 봉상 시편을 만들었다. 분말의 미세조직은 α-AI수지상과 수지상간 편석부로 이루어져 있으며 Mn첨가에 따라 조직의 변화는 관찰되지 않았다. 빠른 냉각속도로 인하여 2.0%Mn을 첨가한 경우에도 초정 Mn상을 발견할 수 없었다. 압출재의 미세조직은 아결정립으로 이루어져 있으며 약간의 제2상들이 관찰되었다. 대부분의 Mn 분산상은 압출후 용체화처리 과정에서 형성되었으며 시효경화량은 Mn양에 관계없이 일정하였다. 460˚C에서 1시간 용체화처리하고 120˚C에서 24시간 시효처리한 경우 최대의 시효경도값을 나타내었다. 인장강도는 Mn첨가량에 따라 증가 하였는데 이것은 Mn분산상의 밀도증가에 의한 것으로 확인되었다. 2.0%Mn을 첨가한 합금의 시효후 인장강도는 590MPa, 연산율은 4%를 보였다.