When the concrete is subjected to impact of the projectile, compressive stress wave is transmitted to the rear side. When the compressive stress wave reached the rear side, is was reflected as a tensile wave. And, when the tensile stress in the concrete matrix exceeded the dynamic tensile strength, crack in the concrete was occurred.

Fracture behavior of concrete subjected to dynamic loading is affected by loading rate and strain rate. In this study, compressive strength properties according to strain rate of fiber reinforced concrete by rapid loading with 500ton rapid loading test machine was analyzed.

In this study, rear failure properties of fiber reinforced concrete considering projectile type was evaluated. It was considered that scabbing of Flat nose projectile reduced more than sperical nose projectile by dispersion of impact force.

본 연구는 폴리비닐 알코올 섬유 및 강섬유를 체적비율로 1.5% 혼입한 고인성 섬유보강 시멘트복합체에 대한 비상체의 고속충돌시험을 실시하고, 충돌조건에 따른 파괴특성을 실험적으로 검토하는 것을 목적으로 하였다. 비상체의 충돌에 의한 고인성 섬유보강 시멘트복합체의 파괴특성을 평가하기 위하여 화약압력식 충격시험장치를 활용하였으며, 충돌속도의 범위는 약 150 ~ 1,000m/s로 설정하였다. 파괴특성에 대한 평가결과, 고인성 섬유보강 시멘트복합체는 섬유를 혼입하지 않은 Plain시험체의 약 3배 이상의 비상체 운동에너지가 작용하는 범위에서도 표면관입의 파괴등급으로 평가되었으며, 시험체가 파단되지 않는 내충격성능이 확인 되었다. 또한, 충돌시험 전후에 대한 시험체의 질량감소율의 경우, Plain시험체는 비상체의 운동에너지의 증가율과 비례적인 관계를 보였지만, 고인성 섬유보강 시멘트복합체는 비상체의 운동에너지의 영향을 크게 받지 않는 것으로 나타났다. 특히, 이와 같은 경향은 시험체 배면의 파괴특성과 밀접한 관계를 가지며, S시험체에 비해 PVA시험체의 배면박리 억제효율이 큰 것으로 평가되었다. 한편, 국부손상에 대한 표면관입깊이 및 배면박리깊이의 관계를 검토한 결과, 고인성 섬유보강 시멘트복합체는 Plain과 달리 시험체 단면의 중앙선을 기준으로 배면에 가까운 영역에서 배면박리가 발생하는 것을 알 수 있었다. 본 연구를 통해 비상체의 충돌에 대한 고인성 섬유보강 시멘트복합체의 주요 파괴거동이 검토되었으며, Plain과 비교하여 내충격성능의 향상을 명확히 확인하였다.

Shock wave caused by the high-velocity impact causing the tensile strain and stress on the rear side. When the tensile strain and stress exceeds the tensile strength of the concrete, crack and fracture were occurred. The strain on the rear side was reduced due to Improvement of the tensile strength by fiber reinforcement and increasing the specimen thickness.

Concrete subjected to dynamic loading shows local failure and it can be suppressed by improvement of flexural toughness with reinforced of fiber. Since bonding properties of fiber with matrix, specific surface area and numbers of fiber are different by fiber reinforcement type, mechanical properties of fiber reinforced concrete and improvement of impact resistance performance need to be considered. In this study, improvement mechanical properties by dynamic lodaing have been evaluated according to SF, PA fiber.

Tensile stress and strain of rear by shock wave become the cause of rear side scabbing of concrete subjected to high-velocity impact. Improvement of flexural and tensile performance by fiber reinforcement has great effect on the suppression of the rear scabbing.

In this study, local fracture of concrete was evaluated through high-velocity impact test. As results, increase of bending tension performance by fiber reinforcement did not affect penetration depth Control, but it decreased rear side fracture thickness and diameter. Therefore, it was observed that fiber reinforcement decreases scabbing limit thickness.

In this study, impact of high-velocity projectile by mixing steel fiber, polyamide, nylon, polyethylene fiber which have different shape and properties respectively. Scabbing is restrained because of micro-crack caused by the shock wave offset effect and energy dispersive of synthetic fibers are mixed populations.

본 연구에서는 섬유종류에 따른 인발특성과 섬유보강 콘크리트의 휨특성에 대하여 평가하기 위하여, 섬유의 재질 및 형상 다른 후크형강섬유, 비정질 강섬유 및 폴리아미드 섬유에 대하여 인발시험과 섬유보강 콘크리트 시험체를 제작하여 휨특성을 평가하였다. 그 결과, 후크형 강섬유의 경우 최대인발하중에서 섬유가 매트릭스로부터 인발되었지만, 비정질 강섬유는 섬유와 매트릭스의 부착강도가 섬유자체의인장강도보다 높아 섬유가 매트릭스로부터 인발되지 않고 파괴되는 현상을 나타내었다, 한편, 폴리아미드 섬유는 연신율에 의해 최대인발하중까지 변위가 크게 발생하였으며, 최대하중이후에 섬유가 끊어지는 파괴특성을 나타내었다. 섬유보강 콘크리트의 휨특성에 있어서 비정질 강섬유는 매트릭스와의 부착강도가 높고, 섬유의 혼입개체수가 많아 콘크리트의 최대휨강도는 높았지만, 균열발생 이후 섬유가 매트릭스로부터 인발되지 않고 섬유가 파괴되는 것에 의해 응력의 저하가 급격하게 발생하지만, 후크형 강섬유보강 콘크리트는 균열발생 이후 섬유가 인발되면서 응력의 저하가 완만하게 발생하였다. 폴리아미드 섬유보강 콘크리트는 균열발생이후 섬유의 연신률에 의해 응력이 급격하게 저하하는 구간이 발생하였으며, 섬유와 매트릭스의 부착에 의해 재상승하였다가 섬유가 끊어지면서 파괴되었다. 섬유와 매트릭스의 인발특성은 섬유보강 콘크리트의 휨강도 및 변형 능력에 큰 영향을 미치는 것으로 판단된다.