Nano-sized WC powders were synthesized by vapor phase reaction using the precusor of tungsten ethoxide under helium and hydrogen atmosphere. The phases of the powder were varied with reaction Bone and gas flow rate. The powder size was about 30nm in diameter, and the tungsten carbide powder was coated by carbon layer. The synthesis of nano-sized WC powders was promoted as the hydrogen gas flow rate became higher. Inversely, tungsten oxide was formed by increasing the flow rate of helium gas. The synthesized powders were analyzed by XRD, FE-SEM, carbon analyzer etc.

Fe-Co nanocomposite powders with different composition were prepared by chemical vapor condensation (CVC) process and their characterizations were studied by means of X-ray diffraction, transmission electron microscopy, and vibrating sample magnetometer. The particles having the mean size of 5~25 nm consisted of metallic cores and oxide shells. The Co contents and particle size increased with increasing the carrier gas flow rate of Co precursor. The saturation magnetization and coercivity increased with increasing Co content. and the saturation magnetization maximized at the 40 wt.%Co. The Fe-Co nanocomposite powder oxidized at showed the maximum coercivity of 1739 Oe.

In this study, the WC-10 wt.%Co nanopowders doped by grain growth inhibiter were produced by three different methods based on the spray conversion process. Agglomerated powders with homeogenous distribution of alloying elements and with internal particles of about 100-200 nm in diameter were synthesized. The microstructural changes and sintering behavior of hardmetal compacts were compared with doping method and sintering conditions. The microstructure of hardmetals was very sensitive to doping methods of inhibitor. Nanostructured WC-Co hardmetal powder compacts containing TaC/VC doped by chemical method instead of ball-milling shown superior sintering densification, and the microstructure maintained ultrafine scale with rounded WC particles.

나노미터 크기의 결정립을 가지는 나노분말 및 나노복합분말의 제조와 특성에 관한 연구가 매우 활발하다. 나노복합분말의 제조방법에는 기상증발후 응축법, 화학응축법, 기계적합금법 등이 있으나, 고순도 및 균일한 크기분포의 분말과 응집되지 않은 분말의 제조 조건을 가장 잘 만족하는 방법은 화학기상응축법(Chemical Vapor Condensation; CVC)이다. 본 연구그룹 에서는 CVC밤법으로 이용하여 공구/금형재료에 가장 많이 사용되는 WC/Co 합금

공구강 등 산업용 재료로 널리 사용되는 카바이드 계 재료는 입자 크기 및 분포에 따라 기계적 성질이 변화하므로, 이를 제어하고 조절하는 기술에 관하여 많은 연구가 진행되어 왔다. 본 연구에서는 TiCN-WC-Co 복합초경계 에서 소결 공정 및 조성변화에 따른 입자 모양을 관찰하고 이에 따른 업자 성장 거동을 고찰하였다. 일반적으로 입자 조대화 양상과 고상 입자의 모양과는 밀접한 관계가 있다. 각진 입자의 경우에 는 계면이 원자적으로 singular 하여