We combined Field-Activated Combustion Synthesis(FACS) with mechanical pressure to produce dense WC-20 vol.%Co composite in one step. The hardness, the fracture toughness and the relative density of the dense WC-20 vol.%Co were investigated. Under the application of 60 MPa pressure and 3000A current on the reactants, the relative density of WC-20 vol.%Co composite was 99.4%. The fracture toughness and hardness were and respectively. The fracture toughness and hardness of WC-20 vol.%Co composite produced by FAPACS were lower than that of nanostructured composite, but similar to commercial ones. Therefore we concluded that the FAPACS method which can produce WC-20 vol.%Co within several minutes in one step is superior to conventional ones.

Ti5Si3와 Ti5Si3-ZrO2 복합재료의 연소합성에 미치는 전기장의 영향에 관하여 연구하였다. 45mole% 이상 첨가한 Ti5Si3-ZrO2 복합재료는 전기장하에서만 연소합성할 수 있었다. Ti5Si3-45mole% ZrO2와 Ti5Si3-60mole% ZrO2 복합재료는 전기장을 가하지 않은 상태에서는 불안정한 연소파가 전파되었지만 반응은 완전히 일어나지 않았다 즉, 불안정한 연소파는 시편의 중앙 부근까지 전파 된 후 멈추었다. Ti5Si3-ZrO2 복합재료의 연소파 속도는 시편에 가해준 전기장에 의해 약간 증가하였다.

Fe78B13Si9 비정질 합금의 결정화 거동과 취성 현상을 시차열량기 시험, x-선회절시험 및 투과 전자현미경 관찰을 통해서 조사 연구하였다. 결정화는 두단계의 발열반응으로 진행되었으며, 첫번째 단계에서는 비정질로부터 B.C.C. 구조인 α-(Fe, Si)의 수지상이 생성되었고, 두번째 단계에서는 남아있던 비정질로부터 B.C.T 구조인 Fe2B가 형성되었다. 에닐링 온도에 따른 시편의 파단과 변형율은 비정질 상태인 약 340˚C부터 급긱히 감소하였다.