Dense -20vol.%SiC composite was synthesized by high-frequency induction-heated combustion synthesis(HFIHCS) method within 2 minutes in one step from elemental powder mixture of W, Si and C. Simultaneous combustion synthesis and densification were accomplished under the combined effects of an induced current and mechanical pressure. Highly dense -20vol.%SiC with relative density of up to 97% was produced under simultaneous application of 60MPa pressure and the induced current. The average grain size of was about 5.2. The hardness and fracture toughness values obtained were 1700kg/ and , respectively.

WC and dense WC-10 vol%Co materials with grain size of~1 were synthesized by high-frequency induction heated combustion synthesis (HFIHCS) method in one step from elemental powders of W, C and Co within several minutes. Simultaneous combustion synthesis and densification were accomplished under the combined effects of an induced current and mechanical pressure. In the absence of cobalt additive, WC can be formed, but its relative density was low (about 73%) under simultaneous application of a 60 MPa pressure and the induced current. However, in the presence of 10 vol.%Co, the relative density increased to 99% under the same experimental condition. The percentages of the total shrinkage occurring before and during the synthesis reaction of WC-10 vol.%Co were 5% and 51%, respectively. The fracture toughness and hardness values of WC-10 vol.%Co were 10 MPa . m and 1840 kg/, respectively.