Ti-Al-Si target and Cr-Si target are sputtered alternately to develop a multi-layered nitride coating on a steel mold to improve die-casting lifetime. Prior to the multi-layer deposition, a CrN layer is developed as a buffer layer on the mold to suppress the diffusion of reactive elements and enhance the cohesive strength of the multi-layer deposition. Approximately 50 nm CrSiN and TiAlSiN layers are deposited layer by layer, and form about three μm-thickness of multi-layered coating. From the observation of the uncoated and coated steel molds after the acceleration experiment of liquid metal injection casting, the uncoated mold is severely eroded by the adhesion of molten metallic glass. On the other hand, the multi-layer coating on the mold prevents element diffusion from the metallic glass and mold erosion during the experiment. The multi-layer structure of the coating transforms the nano-composite structured coating during the acceleration test. Since the nano-composite structure disrupts element diffusion to molten metallic glass, despite microstructure changes, the coating is not eroded by the 1,050 oC molten metallic glass.

우리나라의 국회의원은 대부분 선거구 단위로 선출되기 때문에 선거는 지리학의 주요 관심대상이 된다. 이 연구의 주된 목적은 수도권을 사례지역으로 하여 19대 및 20대 국회의원 선거 결과에서 나타난 공간 패턴의 변화 양상을 분석하는 것이다. 이를 위해서 읍면동 단위의 지역구 및 비례대표 선거 결과 데이터에 대해 공간통계 분석을 수행하였는데, 주요 결과는 다음과 같다. 첫째, 지역구와 비례대표 모두 여당의 득표율이 상당히 줄었지만, 양당 기준 하에서의 여당의 총 득표율, 그리고 최다득표동의 수 및 득표율은 큰 변화가 없는 것으로 나타났다. 둘째, 각 시점 별 여당 득표율의 공간 군집성을 분석한 결과 읍면동 단위가 선거구 단위에 비해, 비례대표 선거가 지역구 선거에 비해 더 강한 공간 군집성을 보였다. 서울 남동부 및 경기도 외곽에서 득표율이 높은 반면 서울의 여타 지역 및 서울 인접 지역에서는 득표율이 낮은 패턴이 대체로 유지되면서 시점 간에 전역적인 공간 군집성은 큰 변화가 없었으나 국지적으로는 지역구와 비례대표 모두 다소 간의 변화가 나타났다. 셋째, 두 시점 간의 여당 득표율의 공간적 상관성을 분석한 결과 대체로 정치적 성향을 유지하는 경향이 우세하였다. 읍면동 기준으로 약 30%는 공간 군집을 이루면서 정치 성향을 유지하는 경향이 강한 것으로 나타났는데, 득표율의 변화가 발생한 지역 또한 강한 공간 군집성을 나타내었다